D1451 radiation curable supercoatings for multi-mode optical fiber

ABSTRACT

The first aspect of the instant claimed invention is a method of formulating radiation curable Supercoatings for application to an optical fiber used in a telecommunications network. A Multi-layer Film Drawdown Method useful in the Method of formulating radiation curable Supercoatings is also described and claimed. Single mode Optical fibers coated with specific radiation curable Supercoatings are also described and claimed.

RELATED PATENT APPLICATIONS

This patent application claims priority to U.S. Provisional Patent Application 61/272,596, filed Oct. 9, 2009 and to U.S. Provisional Patent Application 61/250,329, filed Oct. 9, 2009, U.S. Provisional Patent Application 61/287,567, filed Dec. 17, 2009 and U.S. Provisional Patent Application 61/363,965, filed Jul. 13, 2010, which are all incorporated by reference in their entirety.

FIELD OF THE INVENTION

The present invention relates to radiation curable coatings for optical fiber.

BACKGROUND OF THE INVENTION

An optical fiber is a glass fiber that carries light along its length. Optical fibers are widely used in fiber-optic communications, which permits transmission over longer distances and at higher bandwidths (data rates) than other forms of communications. Fibers are used instead of metal wires because signals travel along them with less loss, and they are also immune to electromagnetic interference.

Light is kept in the core of the optical fiber by total internal reflection. This causes the fiber to act as a waveguide. Fibers which support many propagation paths or transverse modes are called multi-mode fibers (MMF), while those which can only support a single mode are called single-mode fibers (SMF). MMF generally have a larger core diameter, and are used for short-distance communication links and for applications where high power must be transmitted. SMF are used for most communication links longer than 550 meters (1,800 ft).

Throughout this patent application, attenuation in fiber optics, also known as transmission loss, is defined as the reduction in intensity of the light beam (or signal) with respect to distance traveled through a transmission medium. Attenuation loss coefficients in optical fibers usually are reported using units of decibels per kilometer, abbreviated dB/km.

Attenuation is an important factor limiting the transmission of a digital signal across large distances. Thus, much research has gone into both limiting the attenuation and maximizing the amplification of the optical signal. Empirical research has shown that attenuation in optical fiber is caused primarily by both scattering and absorption.

In 1965, Charles K. Kao {one of three winners of the 2009 Nobel Prize in physics for “groundbreaking achievements concerning the transmission of light in fibers for optical communication”} and George A. Hockham of the British company Standard Telephones and Cables (STC) were the first to promote the idea that the attenuation in optical fibers could be reduced below 20 decibels per kilometer (dB/km), allowing optical fibers to be a practical medium for communication. They proposed that the attenuation in fibers available at the time was caused by impurities, which could be removed, rather than fundamental physical effects such as scattering. The crucial attenuation level of 20 dB/km was first achieved in 1970, by researchers Robert D. Maurer, Donald Keck, Peter C. Schultz, and Frank Zimar working for American glass maker Corning Glass Works, now Corning Incorporated. They demonstrated a fiber with 17 dB/km attenuation by doping silica glass with titanium. A few years later they produced a fiber with only 4 dB/km attenuation using germanium dioxide as the core dopant. The achievement of such low attenuations ushered in optical fiber telecommunications and enabled the internet.

The following U.S. patent is incorporated by reference in its entirety: U.S. Pat. No. 6,014,488 issued on Jan. 11, 2000.

Microbends are sharp but microscopic curvatures in an optical fiber involving local axial displacements of a few micrometers and spatial wavelengths of a few millimeters. Microbends can be induced by thermal stresses and/or mechanical lateral forces. When present, microbends attenuate the signal transmission capability of the coated optical fiber. Thus for the success of a telecommunications network it is known each telecommunications system has a limit to the amount of tolerable increase in attenuation for optical fiber and that to avoid reaching that limit it is well to reduce microbending overall because reducing microbending, reduces the increase in attenuation.

One of the critical driving forces for the development of optical fiber coating technology is increased user demands on videos. For the existing technology of optical fiber coating, 2G network application is sufficient. However, the future networks, such as 3G, 4G, and IPTV, high definition television (HDTV), video conferencing and other high bandwidth applications will impose a higher requirement for the performance of optical fiber, therefore the requirement of performance of the optical fiber coating will become higher and higher.

In order to meet the huge demand of video applications on the internet, the telecommunication network of next generation requires the support of transmission of greater capacity, longer distance and broader spectral range, and the performance of the current generation of optical fibers G652 was developed for long haul straight alignment utility; therefore G562 is not suitable to meet the requirements of Fiber to the Home (FTTH) challenges.

As optical transport of communication signals migrates into homes and MDU's (Multiple Dwelling Units), optical glass fibers are encountering tighter bends, requiring optical fiber producers to offer G657 Macrobend resistant fibers. At the same time, increasing demands for bandwidth are putting strains on the available margin in deployed networks.

The first generation of radiation curable DeSolite Radiation curable Supercoatingsm (trademark of DSM IP Assets B.V.) for optical fiber are described and claimed in these U.S. patent applications, which are hereby incorporated by reference in their entirety: U.S. patent application Ser. No. 11/955,935, filed Dec. 13, 2007, published as US 20080226916 on Sep. 19, 2008; U.S. patent application Ser. No. 11/955,838, filed Dec. 13, 2007, published as US 20080241535 on Oct. 23, 2008; U.S. patent application Ser. No. 11/955,547, filed Dec. 13, 2007, published as US 20080226912 on Sep. 19, 2008; U.S. patent application Ser. No. 11/955,614, filed Dec. 13, 2007, published as US 20080226914 on Sep. 19, 2008; U.S. patent application Ser. No. 11/955,604, filed Dec. 13, 2007, published as US 20080226913 on Sep. 19, 2008;

U.S. patent application Ser. No. 11/955,721, filed Dec. 13, 2007, published as US 20080233397 on Sep. 25, 2008; U.S. patent application Ser. No. 11/955,525, filed Dec. 13, 2007, published as US 20080226911 on Sep. 19, 2008; U.S. patent application Ser. No. 11/955,628, filed Dec. 13, 2007, published as US 20080226915 on Sep. 19, 2008; and U.S. patent application Ser. No. 11/955,541, filed Dec. 13, 2007, published as US 20080226909 on Sep. 19, 2008.

U.S. patent application Ser. No. 11/955,541, filed Dec. 13, 2007, published on Sep. 18, 2009 as US Published Patent Application 20080226909, entitled “D1381 RADIATION CURABLE SUPERCOATINGS FOR OPTICAL FIBER” describes and claims Radiation Curable Supercoatings for Optical Fiber as follows:

Supercoatings suitable for coating an optical fiber;

wherein the Supercoatings comprise at least two layers, wherein the first layer is a Primary Coating that is in contact with the outer surface of the optical fiber and the second layer is a Secondary Coating in contact with the outer surface of the Primary Coating,

wherein the cured Primary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity:

A) a % RAU of from about 84% to about 99%;

B) an in-situ modulus of between about 0.15 MPa and about 0.60 MPa; and

C) a Tube Tg, of from about −25° C. to about −55° C.;

wherein the cured Secondary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity:

A) a % RAU of from about 80% to about 98%;

B) an in-situ modulus of between about 0.60 GPa and about 1.90 GPa; and

C) a Tube Tg, of from about 50° C. to about 80° C.

With the recent launch of the DeSolite Supercoatings™ line of Radiation curable Supercoatings for optical fiber, by DSM Desotech, see www.Supercoatines.com it has been reported that use of Supercoatings has great positive effect upon the microbending characteristics of the optical fiber. Thus using Supercoatings is known to reduce the amount of microbending in an optical fiber and reducing the amount of microbending reduces the amount of attenuation in the telecommunications network

As the demand for ever increasing bandwidth develops in the internet and current telecommunications devices, the demand for optical fiber that is attenuation resistant will also increase. Thus the demand for radiation curable Supercoatings will increase. As the demand for attenuation resistant optical fiber and radiation curable Supercoatings increases it would be desirable to have a method for selecting and formulating radiation curable Supercoatings for optical fiber.

SUMMARY OF THE INVENTION

The first aspect of the instant claimed invention is a method of formulating radiation curable Supercoatings for application to an optical fiber used in a telecommunications network, wherein said Supercoatings comprise at least two layers, the first layer being a primary coating that is in contact with the outer layer surface of the optical fiber and the second layer being a secondary coating in contact with the outer surface of the primary coating, wherein the cured primary coating on the optical fiber has the following properties after initial cure and after at least one month aging at 85° C. and 85% relative humidity:

-   1) a % RAU of from about 84% to about 99%; -   2) an in-situ modulus of between about 0.15 MPa and about 0.60 MPa;     and -   3) a Tube T, of from about −25° C. to about −55° C.;     and wherein the cured secondary coating on the optical fiber has the     following properties after initial cure and after at least one month     aging at 85° C. and 85% relative humidity: -   4) a % RAU of from about 80% to about 98%; -   5) an in-situ modulus of between about 0.060 GPa and about 1.90 GPa;     and -   6) a Tube T_(g) of from about 50° C. to about 80° C.;     said method comprising the steps of: -   a) determining the Maximum Acceptable Increase in Attenuation     requirements for the telecommunications network where the optical     fiber will be installed; -   b) determining a Field Application Environment of the Supercoatings     comprising:     -   i) selecting the type of glass being used in the optical fiber;     -   ii) deciding whether the secondary coating of the Supercoatings         will be applied over the primary coating of the Supercoatings         wet-on-dry or wet-on-wet;     -   iii) selecting the type, number of lights and positioning of         lights along a draw tower manufacturing line that are used to         cure the Supercoatings on the optical fiber; and     -   iv) selecting the line speed at which the Supercoatings will be         applied; -   c) formulating a primary coating composition in a liquid, uncured     state; -   d) formulating a secondary coating composition in a liquid, uncured     state; -   e) using a Three-Dimensional Laced Methodology, as shown in FIGS. 2,     3 and 4, of     -   i) testing the primary coating and secondary coating of the         Supercoatings to determine if the Supercoatings parameters 1)         through 6) are achieved; wherein         -   if each and every one of the Supercoatings parameters 1)             through 6) are achieved then proceed to step 1); and         -   if each and every one of the Supercoatings parameters 1)             through 6) have not been achieved, reformulate either or             both of the primary coating or secondary coating of the             Supercoatings and repeat step ii) until each and every one             of the Supercoatings parameters 1) through 6) are achieved;             and then     -   ii) verifying the integrity of the reformulation of the primary         coating and the secondary coating of the Supercoatings by         evaluating changes in each formulation relative to the other         formulation and relative to all of the Supercoatings         parameters 1) through 6); -   f) using the results from step e)i) and step e)ii) to finalize the     selection of Supercoatings to achieve the Maximum Acceptable     Increase in Attenuation of the coated optical fiber.

The second aspect of the instant claimed invention is the Method of the first aspect, in which the Three-Dimensional Laced Methodology includes using a Multi-Layer Film Drawdown method to evaluate composite fused Primary Coating Layer and Secondary Coating Layer of Radiation curable Supercoatings.

The third aspect of the instant claimed invention is a Multi-Layer Film Drawdown Method comprising the steps of:

-   a) selecting a substrate for the test; -   b) applying a Primary coating to the substrate using a defined     thickness drawdown bar; -   c) optionally curing the Primary coating; -   d) applying a Secondary coating to the Primary coating using a     defined thickness drawdown bar, wherein the defined thickness of the     drawdown bar to apply the Secondary coating is greater than the     defined thickness of the drawdown bar used to apply the primary     coating; -   e) applying radiation to the multi-layer film sufficient to     effectuate the cure of both the Primary and Secondary into a Fused     Composite film; -   f) removing the film from the substrate; and -   g) evaluating the functional properties of the cured film.

The fourth aspect of the instant claimed invention is a single-mode optical fiber coated with Supercoatings, wherein said Supercoatings comprise,

-   -   a Primary Coating Layer and a Secondary Coating Layer;     -   wherein the composition of the Primary Coating layer, prior to         curing, is selected from the group consisting of the         formulations of Examples 1PA2, 1PB3, 1PC1, 1PD5, 2Alpha, and         2Beta;     -   wherein the composition of the Secondary Coating layer, prior to         curing, is selected from the group     -   consisting of the formulations of Examples 2SA4 and 2SB3 and         3SA1 and 5SA1.

The fifth aspect of the instant claimed invention is a multi-mode optical fiber coated with radiation curable coatings comprising a Primary Coating Layer and a Secondary Coating Layer

-   -   wherein the composition of the Primary Coating layer, prior to         curing, is selected from the group     -   consisting of the formulation of Example 1PD5; and     -   wherein the composition of the Secondary Coating layer, prior to         curing, is selected from the group     -   consisting of the formulations of Examples 2SA4 and 2SB3 and         3SA1 and 5SA1.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram of historical depiction of formulation diagram for how typical formulating for optical fiber coatings has been done—illustrating the prior art. This is a comparative example, not an example of the instant claimed invention.

FIG. 2 is the first embodiment illustrating the three-dimensional laced methodology for formulating radiation curable Supercoatings for Optical Fiber.

FIG. 3 is the second embodiment illustrating the three-dimensional laced methodology for formulating radiation curable Supercoatings for Optical Fiber.

FIG. 4 is the third embodiment illustrating the three-dimensional laced methodology for formulating radiation curable Supercoatings for Optical Fiber.

FIG. 5 is an illustration of the results of the Multi-Layer Film Drawdown method showing a colored photograph of a Supercoatings Primary Layer, drawn down with a 1.5 mil bar, then a candidate for Supercoatings Secondary layer, observed as a brown layer, is drawn down over the primary with a 3 mil bar, and the whole plate cured.

FIG. 6 is Spectra “all”, which shows 4 spectra with a comparable appearance to two sets of two sitting on top of each other.

FIG. 7 is Spectra “Brown” shows the colored secondary portion only, and the top of the dual drawdown portion. The two spectra match up quite well.

FIG. 8 is Spectra “for the Supercoatings Primary Layer from Example 1PC1” shows the glass side of the dual layer, and the glass side of a single 3 mil, Example 1PC1 Supercoatings Primary Layer drawdown. Again the spectra match up very well.

FIG. 9 is a DMA plot of a Flat Film Drawdown of Primary PMoct Supercoatings Candidate, this is a Comparative Example, not an Example of the Instant Claimed Test Method.

FIG. 10 is a DMA plot of a Flat Film Drawdown of Secondary PMoct, Supercoatings Candidate, this is a Comparative Example, not an Example of the Instant Claimed Test Method.

FIG. 11 is a DMA plot of a Tube of Secondary PMoct, Supercoatings Candidate over Primary PMoct Supercoatings as put on wire using the Draw Tower Simulator; this is a Comparative Example, not an Example of the Instant Claimed Test Method.

FIG. 12 is a Dynamic Mechanical Analysis (“DMA”) plot of composite film of PMoct Primary (Example 1PB3) covered by PMoct Secondary (Example 2SB3) applied Wet-on-Wet (abbreviated W-O-W).

FIG. 13 is a DMA plot of composite film of PMoct Primary (Example 1PB3) covered by PMoct Secondary (Example 2SB3) applied Wet on Dry (abbreviated W-O-D).

DETAILED DESCRIPTION OF THE INVENTION

The first aspect of the instant claimed invention is a method of formulating radiation curable Supercoatings for application to an optical fiber used in a telecommunications network, wherein said Supercoatings comprise at least two layers, the first layer being a primary coating that is in contact with the outer layer surface of the optical fiber and the second layer being a secondary coating in contact with the outer surface of the primary coating, wherein the cured primary coating on the optical fiber has the following properties after initial cure and after at least one month aging at 85° C. and 85% relative humidity:

1) a % RAU of from about 84% to about 99%;

2) an in-situ modulus of between about 0.15 MPa and about 0.60 MPa; and

3) a Tube T_(g), of from about −25° C. to about −55° C.;

and wherein the cured secondary coating on the optical fiber has the following properties after initial cure and after at least one month aging at 85° C. and 85% relative humidity:

4) a % RAU of from about 80% to about 98%;

5) an in-situ modulus of between about 0.060 GPa and about 1.90 GPa; and

6) a Tube T, of from about 50° C. to about 80° C.;

said method comprising the steps of:

a) determining the Maximum Acceptable Increase in Attenuation requirements for the telecommunications network where the optical fiber will be installed;

b) determining a Field Application Environment of the Supercoatings comprising:

i) selecting the type of glass being used in the optical fiber;

ii) deciding whether the secondary coating of the Supercoatings will be applied over the primary coating of the Supercoatings wet-on-dry or wet-on-wet;

iii) selecting the type, number of lights and positioning of lights along a draw tower manufacturing line that are used to cure the Supercoatings on the optical fiber; and

iv) selecting the line speed at which the Supercoatings will be applied;

c) formulating a primary coating composition in a liquid, uncured state;

d) formulating a secondary coating composition in a liquid, uncured state;

e) using a Three-Dimensional Laced Methodology, as shown in FIGS. 2, 3 and 4, of

i) testing the primary coating and secondary coating of the Supercoatings to determine if the Supercoatings parameters 1) through 6) are achieved; wherein

-   -   if each and every one of the Supercoatings parameters 1)         through 6) are achieved then proceed to step f); and     -   if each and every one of the Supercoatings parameters 1)         through 6) have not been achieved, reformulate either or both of         the primary coating or secondary coating of the Supercoatings         and repeat step ii) until each and every one of the         Supercoatings parameters 1) through 6) are achieved; and then

ii) verifying the integrity of the reformulation of the primary coating and the secondary coating of the Supercoatings by evaluating changes in each formulation relative to the other formulation and relative to all of the Supercoatings parameters 1) through 6);

f) using the results from step e)i) and step e)ii) to finalize the selection of Supercoatings to achieve the Maximum Acceptable Increase in Attenuation of the coated optical fiber.

The first step in the process is determining the Maximum Acceptable Increase in Attenuation requirements for the telecommunications network where the optical fiber will be installed. Determining the attenuation requirements for the telecommunications network involves the design criteria for the Optical Fiber Network. Some considerations in the design include: an understanding of how much of the network is straight line installation of multi-mode optical fiber as compared to how much of the network is Fiber-to-the-Home (abbreviated FFTH) installation of single mode optical fiber. There are many other design criteria for an Optical Fiber network that are known to people of ordinary skill in the art of designing Optical Fiber Networks.

Specific Considerations in design of Optical Fiber Networks include the following

It is currently known, that in contrast to traditional straight line optical fiber long haul networks, that FTTH applications have to work at least at three wavelengths:

-   -   1310 nm (data/voice upstream)     -   1490 nm (data/voice downstream)     -   1550 nm (video signal).         Traditional optical fiber networks used Standard single mode         wavelengths of between 1310 nm and 1550 nm, with the wavelength         of 1625 nm being available for testing of the system. Now, with         the increasing demand for signal transmission it is anticipated         that future optical fiber networks will have to be able to         transmit signal containing actual data at 1310 nm, 1550 nm and         1625 nm. Optical fiber networks incorporating fiber that can         transmit at all three of these wavelengths are known to be more         vulnerable to both Macrobending and Microbending. Microbending         is known to be more damaging to transmission at a 1625         wavelength.

There are several sources for the standards for attenuation in the telecommunications industry. One such standards setting organization is The Telecommunications Industry Association (TIA), which is the leading trade association representing the global information and communications technology (ICT) industries through such activities such as: Standards development, Providing Market Intelligence, Government affairs guidance, Certification of optical fiber and networks containing optical fiber and advice regarding World-wide environmental regulatory compliance. TIA's United States Technical Advisory Groups (USTAG) also participates in international standards-setting activities, such as the International Electrotechnical Commission (IEC).

Another source for the standards for attenuation in the telecommunications industry is the IEC. The International Electrotechnical Commission (IEC) is the leading global organization that prepares and publishes international standards for all electrical, electronic and related technologies. These serve as a basis for national standardization and as references when drafting international tenders and contracts.

Telcordia is a U.S. based corporation that provides fiber optic media & components analysis & consulting services. They also write and keep a library of Generic Requirements for Optical Fiber.

All of these organizations have publicly available literature, reports and standards that are used by people of ordinary skill in the art of designing optical fiber networks.

Methods used to test for microbending sensitivity are described in IEC TR 62221, First Edition 10-2001. There are currently four test methods used to determine microbending sensitivity, which is reported in attenuation units of dB/km.

Method A—Expandable Drum calls for at least 400 m of fiber to be wound with minimal tension around an expandable drum with material of fixed roughness on the drum surface. Method B—Fixed-Diameter Drum calls for at least 400 m of fiber to be wound with 3N tension around a fixed-diameter drum with material of fixed roughness on the drum surface. Method C—Wire Mesh calls for application of wire mesh (under load) to the fiber under Test. Method D—Basketweave calls for 2.5 km of fiber to be applied to a fixed diameter drum via a “basketweave” wrap.

Of these four test methods, only Method D, specifically describes a procedure to measure the microbending sensitivity of fibers as a function of temperature and provides the microbending sensitivity over a wide temperature range and suggests that temperature cycling could include lower temperatures such as −60° C.

Throughout this patent application, microbending sensitivity using test Method D—Basketweave will be spoken of in terms of a dB/Km number, at a specified wavelength and temperature.

There are at least four different types of tests currently in use to test for Microbending Sensitivity with test results being reported in attenuation units of dB/km. Four specific Microbending Sensitivity test Methods are described in IEC TR 62221, First Edition 10-2001.

They are as follows:

-   -   Method A Expandable Drum: Calls for at least 400 m of fiber to         be wound with minimal tension around an expandable drum with         material of fixed roughness on the drum surface.     -   Method B Fixed-diameter drum: Calls for at least 400 m of fiber         to be wound with 3N tension around a fixed-diameter drum with         material of fixed roughness on the drum surface.     -   Method C Wire Mesh: Calls for application of wire mesh (under         load) to the fiber under Test.     -   Method D Basketweave: Calls for 2.5 km of fiber to be applied to         a fixed diameter drum via a “basketweave” wrap.

Throughout this patent application, Method D measured Microbending Sensitivity will be discussed and reported in units of attenuation which will be spoken of in terms of a dB/Km number, at a specified wavelength and temperature. It is understood that whatever Microbending Sensitivity is given, that the number given is the Maximum Acceptable Increase in Attemuation permissible for that optical fiber in a given telecommunications network.

Of these four test methods, only Method D, specifically describes a procedure to measure the Microbending Sensitivity of fibers as a function of temperature and provides the Microbending Sensitivity over a wide temperature range and suggests that temperature cycling could include lower temperatures such as −60° C.

It is understood, within the industry, that it is unlikely that Optical Fibers in a telecommunications network would be routinely exposed to temperatures as low as −60° C. However, after recent field failures in China, it is also beginning to be understood that having a specification for Microbending Sensitivity for the optical fiber in a telecommunications network at room temperature of approximately 25° C. is not sufficient to protect a telecommunications network from having “dark fiber” develop over the course of a winter where the temperature is below freezing (0° C. or 32° F.) for extended periods of time.

Applicants have chosen to report Microbending Sensitivity as a change in attenuation from a baseline per the IEC procedure; this procedure requires the reporting of change in attenuation be reported at specific wavelengths and a temperature of −60° C. Applicants believe that reporting Microbending Sensitivity data at these extreme temperature conditions will provide a type of “worst case scenario” possibility for Microbending Sensitivity of the coated optical fiber in the field.

It is Applicants' position that if the Microbending Sensitivity properties of the Optical Fiber at the −60° C. level are deemed to be acceptable, then it is reasonable to assume that the performance of the Optical Fiber at room temperature, assuming the same level of mechanical stress, will also be acceptable.

Further to this point, at room temperature Microbending Sensitivity testing it may or may not be possible to identify the difference in Microbending Sensitivity between an Optical Fiber coated with a standard, “non-Supercoatings” coating, because neither Supercoatings or a non-Supercoatings is anywhere near their glass transition temperature (Tg) for the primary coating layer at room temperature.

The difference between an Optical Fiber coated with a standard “non-Supercoatings” coating and an Optical Fiber coated with Supercoatings shows up with Microbending Sensitivity testing at the extreme low temperatures because the standard “non-Supercoatings” Primary Layer exceeds its glass transition temperature at the extreme low temperatures and thus transitions from rubbery state to glassy state. Having the Primary Layer of an Optical Fiber coating being in the glassy state is known to cause an increase in Microbending Sensitivity. In contrast, the Tg of a Supercoatings Primary Layer is much lower and therefore the Primary Layer of Supercoatings remains in the rubbery phase which is better for Microbending Sensitivity.

Another way of explaining the difference between standard “non-Radiation curable Supercoatings” for Optical Fiber and Radiation curable Supercoatings for Optical Fiber is that the combination of fully cured, low modulus and low Tg coatings in the Primary Coating Layer and fully cured, high modulus, high Tg coatings in the Secondary Coating Layer of the Supercoatings leads to acceptable performance under the stress of either extreme temperature or mechanical stress or both temperature and mechanical stress with acceptable performance being gauged by the low level of Microbending Sensitivity which is reflected in the fiber having an acceptable increase in reported attenuation.

In current practice, it is understood that the Telecommunications network generally requests that Optical Fiber be supplied with a known maximum attenuation at 1310 nm and room temperature. This highest tolerable level of attenuation is known to people of ordinary skill in the art of design criteria for Telecommunications networks.

For Optical Fibers coated with Radiation curable Supercoatings, it is possible and desirable to report Microbending Sensitivity at three separate wavelengths and at a very cold (−60° C.) temperature. This data can then be used by the Network designer to understand the limits, and be able to predict failure modes for the network. It is applicants' position that a network containing Optical Fibers coated with standard, “non-Supercoatings” will have much less tolerance to the stress involved from the cable environment of temperature extremes and mechanical forces than will a network containing Optical Fibers coated with Radiation curable Supercoatings. Another factor is that it is believed that using Radiation curable Supercoatings to coat Optical Fiber will provide a Telecommunications network with sufficient data to be able to design without requiring the same “safety margin” as is built in with using standard “non-Radiation curable Supercoatings” to coat Optical Fiber.

The next step in the process is determining the Field Application Environment of the Supercoatings requirements for the telecommunications network where the optical fiber will be installed. The Field Application Environment involves the understanding of four factors:

-   -   i) the type of glass being used in the optical fiber;     -   ii) whether the Supercoatings Secondary Layer will be applied         over the Supercoatings

Primary Layer wet on dry or wet on wet;

-   -   iii) the type, number of lights and positioning of lights along         the draw tower manufacturing line that are used to         -   cure the Supercoatings on the optical fiber; and     -   iv) the line speed at which the Supercoatings will be applied.

Regarding element i): Optical Fiber is known to have standard grades for installation of long haul straight cable. Recently various grades of “bend resistant” Optical Fiber have been developed by Optical Fiber Suppliers such as Corning and Drake and OFS and YOFC and others. These bend resistant Optical Fibers are being deployed in Fiber to the Node (FTTX) and Fiber to the Home (FTTH) applications.

Details about standard grade and Microbend resistant Optical Fibers are available from the Suppliers own literature and websites.

Current commercial Optical Fiber available for sale include: Corning® InfiniCor® optical fibers, Corning® ClearCurve® OM2/OM31/OM4 multimode optical fiber, Corning® ClearCurve® single-mode optical fiber, Corning® SMF-28e® XB optical fiber, Corning® SMF-28® ULL optical fiber,

Corning® LEAF® optical fiber, Corning® Vascade® optical fibers and Corning Specialty Fiber,

Draka BendBright SingleMode (BB), Draka TeraLight Singlemode (TM), Draka TeraLight Ultra Singlemode (TU), Draka BendBright-XS (BX), Draka Enhanced Single Mode, Draka NZDSF-LA Singlemode (LA),

OFS AllWave® Zero Water Peak (ZWP) and newly introduced OFS AllWave FLEXZWP Fibers, OFS LaserWave® Fibers, OFS Access ADVANTAGE™ System. OFS HCS®, OFS FiberWire®, and OFS PYROCOAT® brand technologies, YOFC HiBand GIMM fiber, YOFC High Temperature Fibre (HTF) Series, YOFC HiBand Graded-index Multimode Optical Fiber (50/125 & 62.5/125 um) and others.

Typically fiber to be deployed in straight line applications undergoes less stress, and less microbending than fiber to be deployed in FTTX and FTTH applications. Therefore, the selection of Radiation curable Supercoatings to be applied to fiber for FTTX and FTTH applications is crucial to the performance of FTTX and FTTH optical fiber. Accordingly, whenever the optical fiber to be coated is designated for FTTX and FTTH applications, the Supercoatings must be highly resistant to microbending.

Unique to formulating Supercoatings is just how much of the formulation requirements to achieve the six required properties are dependent upon the Mechanical aspects of the coating of an optical fiber. For example, it is possible to coat a standard grade of Optical Fiber with Supercoatings and obtain a Coated Optical Fiber with desired attenuation properties, but it is also possible to coat a “Bend-Resistant” premium grade of Optical Fiber with a standard, “non. Supercoatings”, and have the result be a coated optical fiber with unacceptable Microbending Sensitivity leading to the failure in achieving the system required tolerable level of attenuation. Therefore, in order to produce an optical fiber with the desired attenuation properties it is desirable, optionally even necessary, for the formulator of Supercoatings to have an understanding of the details of the optical fiber production process. These details include the type of glass, the processing temperature, the atmosphere surrounding the application of coating(s), the line speed, the type of radiation source, typically described as a “curing lamp”, and the location and number of curing lamps along the processing line and whether the secondary coating is applied over the primary coating wet on wet or wet on dry. These types of mechanical aspects to the glass processing have, in the past, not been of interest to the formulator of the Optical Fiber coatings because the formulator focused on the Optical Fiber coatings and the glass manufacturer focused on the glass. As stated previously, without an adequate amount of information about the processing of the glass, it is possible to coat a standard grade of Optical Fiber with Supercoatings and obtain a Coated Optical Fiber with desired Microbending Sensitivity properties, but it is also possible to coat a “Bend-Resistant” premium grade of Optical Fiber with a standard, non-Supercoatings, and have the result be a coated optical fiber without the desired Microbending Sensitivity properties.

Regarding element iii) the type, number of lights and positioning of lights along the draw tower manufacturing line that are used to cure the Supercoatings on the optical fiber; the use of conventional ultraviolet mercury arc lamps to emit ultraviolet light suitable to cure radiation curable coatings applied to optical fiber is well known. Ultraviolet arc lamps emit light by using an electric arc to excite mercury that resides inside an inert gas (e.g., Argon) environment to generate ultraviolet light which effectuates curing. Alternatively, microwave energy can also be used to excite mercury lamps in an inert gas medium to generate the ultraviolet light. Throughout this patent application, arc excited and microwave excited mercury lamp, plus various additives (ferrous metal, Gallium, etc.) modified forms of these mercury lamps are identified as mercury lamps. Conventional ultraviolet mercury arc lamps are the “state-of-the-art” when it comes to curing of radiation curable coatings for optical fiber.

However, the use of ultraviolet mercury lamps as a radiation source suffers from several disadvantages including environmental concerns from mercury and the generation of ozone as a by-product. Further, mercury lamps typically have lower energy conversion ratio, require warm-up time, generate heat during operation, and consume a large amount of energy when compared with Lights that are generated by Light Emitting Diodes “LED”.

Knowing what type of light is going to be used in the curing of the Radiation Curable Supercoatings is critical information because in the production of coated optical fiber, the heat generated by the UV mercury lamps can negatively impact the liquid coating in that if the coating is not formulated to avoid the presence of volatiles, those volatiles may be excited and deposit upon the quartz tube surface, blocking the UV rays from irradiating the liquid coating on the glass fiber which inhibits the curing of the liquid coating to a solid.

In contrast to ultraviolet mercury lamps, light emitting diodes (LEDs) are semiconductor devices which use the phenomenon of electroluminescence to generate light. LEDs consist of a semiconducting material doped with impurities to create a p-n junction capable of emitting light as positive holes join with negative electrons when voltage is applied. The wavelength of emitted light is determined by the materials used in the active region of the semiconductor. Typical materials used in semiconductors of LEDs include, for example, elements from Groups 13 (III) and 15 (V) of the periodic table. These semiconductors are referred to as III-V semiconductors and include, for example, GaAs, GaP, GaAsP, AlGaAs, InGaAsP, AlGaInP, and InGaN semiconductors. Other examples of semiconductors used in LEDs include compounds from Group 14 (IV-IV semiconductor) and Group 12-16 (II-VI). The choice of materials is based on multiple factors including desired wavelength of emission, performance parameters, and cost.

Early LEDs used gallium arsenide (GaAs) to emit infrared (IR) radiation and low intensity red light. Advances in materials science have led to the development of LEDs capable of emitting light with higher intensity and shorter wavelengths, including other colors of visible light and UV light. It is possible to create LEDs that emit light anywhere from a low of about 100 nm to a high of about 900 nm. Currently, known LED UV light sources emit light at wavelengths between about 300 and about 475 nm, with 365 nm, 390 nm and 395 nm being common peak spectral outputs. See textbook, “Light-Emitting Diodes” by E. Fred Schubert, 2^(nd) Edition, © E. Fred Schubert 2006, published by Cambridge University Press.

LED lamps offer advantages over conventional mercury lamps in curing applications. For example, LED lamps do not use mercury to generate UV light and are typically less bulky than mercury UV are lamps. In addition, LED lamps are instant on/off sources requiring no warm-up time, which contributes to LED lamps' low energy consumption. LED lamps also generate much less heat, with higher energy conversion efficiency, have longer lamp lifetimes, and are essentially monochromatic emitting a desired wavelength of light which is governed by the choice of semiconductor materials employed in the LED.

Several manufacturers offer LED lamps for commercial curing applications. For example, Phoseon Technology, Summit UV Honle UV America, Inc., IST Metz GmbH, Jenton International Ltd., Lumios Solutions Ltd., Solid UV Inc., Seoul Optodevice Co., Ltd, Spectronics Corporation, Luminus Devices Inc., and Clearstone Technologies, are some of the manufacturers currently offering LED lamps for curing ink-jet printing compositions, PVC floor coating compositions, metal coating compositions, plastic coating composition, and adhesive compositions.

Regarding element iv) the line speed at which the Supercoatings will be applied, in D1381 RADIATION CURABLE SUPERCOATINGS FOR OPTICAL FIBER, U.S. patent application Ser. No. 11/955,541, filed Dec. 13, 2007, published on Sep. 18, 2009 as US Published Patent Application 20080226909, entitled it is stated that a Supercoating may be applied to single-mode optical fiber at a line speed of between about 750 meters/minute to about 2100 meters/minute. As of the date of filing this patent application, Oct. 8, 2010, the optical fiber industry has now progressed to the point where it is possible to draw single-mode optical fiber at line speeds in excess of 2100 meters/minute. It is also possible to draw single-mode optical fiber at line speeds in excess of 2200 meters/minute. It is also possible to draw single-mode optical fiber at line speeds in excess of 2300 meters/minute. It is believed, without intending to be bound thereby that it may also be possible to draw single-mode optical fiber at line speeds in excess of 2350 meters/minute. It is believed, without intending to be bound thereby, that it may also be not possible to draw single-mode optical fiber at line speeds in excess of 2400 meters/minute.

The next step in the process involves using a Three-Dimensional Laced Methodology Evaluation of candidate Radiation curable Supercoatings by evaluation of the Radiation curable Supercoatings Primary Layer and Secondary Layer. Historically Primary and Secondary coatings for optical fiber were formulated and reformulated according to a two-dimensional diagramed way of formulating. FIG. 1 is a diagram of historical depiction of formulation diagram for how typical formulating for optical fiber coatings has been done-illustrating the prior art.

In FIG. 1, Decision Chart 10 shows the two-dimensional Prior Art approach to formulating optical fiber coatings. In FIG. 1, desirable functional property A is illustrated by circle A, Review Point B represents the test to determine whether the liquid optical fiber coating or the cured coating, either in the form of a flat film or in the form of a tubular coating on the optical fiber, has the desired functional property. If the optical fiber coating does have the desired functional property than the decision tree goes to yes and the inquiry is over. If the optical Fiber coating does not have the desired functional property, the formulator reviews the formulation and determines the change to make, as represented by parallelogram D, and then in rectangle C, the formulation is changed. The functional property is retested at Review Point B, and if the desired functional property is obtained then the inquiry is over. If the desired functional property is not obtained, then the decision tree goes back to the top and other reformulating options by the formulator are considered until the next possible formulation is determined and then the formulation is changed and then the desired functional property is retested. This continues until the desired physical property is obtained.

The possible ways to change the coating are illustrated by the information contained n Table 1A, 1B, 1C, 1D, 1E, 2A, 2B, 2C, 2D, 2E, 1F, 2F, 1G, 2G, 1H, 2H, 1J, and 2J which summarize the state-of-the-art understanding of the ingredients that may or may not be used in formulating Primary and Secondary Radiation Curable Coatings for optical fiber with respect to creating formulations with physical properties of the Primary Coating Layers and Secondary Coating Layers on the Optical Fiber that meet the rigorous criteria of Supercoatings. In addition to the information in the Tables contained herein, additional information may be found in issued patents, published patent applications, scientific papers and other information commonly known to people of ordinary skill in the art of Radiation Curable Coatings for Optical Fiber.

TABLE 1A Choice of Oligomer for Supercoatings-Primary Disadvantages-includes Chemistry of Oligomer Sub-Chemistry, within the undesirable interactions for Supercoatings-Primary category Benefits with other components 1. urethane (meth)acrylate other UV-curable end-groups fast cure, toughness, stability, high viscosity (most commonly used e.g. vinyl ether, versatility, many polyols available, oligomer for optical fiber (meth)acrylamide, vinyl amide ease of manufacture coatings) 2. polyester (meth)acrylate other UV-curable end-groups fast cure, low viscosity, versatility, low elongation, poorer e.g. vinyl ether, many polyols and acids available, hydrolytic stability, (meth)acrylamide, vinyl amide oxidative stability more difficult to manufacture 3. silicone (meth)acrylate other UV-curable end-groups very low Tg, hydrophobic and expensive, specialized e.g. vinyl ether, lipophobic, fast cure, stability, low manufacture, refractive (meth)acrylamide, vinyl amide viscosity index may be too low 4. hydrocarbon (e.g. other UV-curable end-groups very low Tg, hydrophobic, hydrolytic poorer oxidative polybutadiene) e.g. vinyl ether, stability, low viscosity stability, poorer (meth)acrylate (meth)acrylamide, vinyl amide solubility, lipophilic 5. fluorocarbon other UV-curable end-groups low Tg, hydrophobic and lipophobic, expensive, poorer (meth)acrylate e.g. vinyl ether, fast cure, stability, low viscosity solubility, refractive (meth)acrylamide, vinyl amide index may be too low, specialized manufacture 6. thiol-ene various enes including, strong network structure, low odor, shelf stability norbornene, vinyl ether, vinyl viscosity, good cured stability ester, vinyl amide, allyl ether, allyl ester, allyl amide, styrene, alkenes (aliphatic enes are used for low Tg) Disadvantages-includes Sub-Chemistry, within the undesirable interactions Chemistry of Oligomer category Benefits with other components 7. acrylated acrylic polymer Other UV-curable end-groups or copolymer e.g. vinyl ether, (meth) acrylamide, vinyl amide 8. cationic epoxy various cationically curable low shrinkage, good adhesion, low slower cure speed, post groups including glycidyl viscosity, stability curing effect, lower ether, glycidyl ester, vinyl elongation ether, oxetane, hydroxyl (aliphatic materials are used for low Tg)

TABLE 1B Choice of Oligomer for Supercoatings-Primary Selection of Polyol to Disadvantages-includes formulate Urethane Sub-Chemistry, within the undesirable interactions Oligomer category Benefits with other components 1. polyether (most poly(alkylene glycols), hydrolytic stability, flexibility, low oxidative stability commonly used polyol for poly(arylene glycols), viscosity optical fiber oligomers) copolymers with other types of polyols 2. polyester aliphatic, aromatic, linear, oxidative stability higher Tg, poorer branched oxidative stability 3. polycarbonate aliphatic, aromatic, linear, oxidative and hydrolytic stability higher Tg, potential branched crystallinity 4. hydrocarbon aliphatic, aromatic, linear, hydrophobic, good stability poor oxidative stability branched, cyclic, saturated, if unsaturated, unsaturated solubility, lipophilic 5. silicone aliphatic, aromatic, linear, hydrophobic and lipophobic, expensive, refractive branched stability, low viscosity index may be too low 6. fluorocarbon aliphatic, aromatic, linear, hydrophobic and lipophobic, expensive, refractive branched stability, low viscosity index may be too low 7. bio-based Various vegetable, see, nut, Generally low Tg, hydrophobic, good May have lower purity biomass and other plant- stability, sustainable or homogeneity derived polyols

TABLE 1C Choice of Oligomer for Supercoatings-Primary Selection of Isocyanate to Disadvantages-includes formulate Urethane Sub-Chemistry, within the undesirable interactions Oligomer category** Benefits with other components 1. aromatic TDI, MDI faster reaction, low cost yellowing, toxicity 2. aliphatic IPDI, HDI, TMDI low yellowing higher cost, slower reaction 3. alkyl-aryl TMXDI stability higher cost, slower reaction 4. DESMODUR ® W* bis(4- Polyurethane resins based on non-homogenous isomer isocyanotocyclohexyl) *Desmodur ® W diisocyanate have blending may lead to methane a high degree of flexibility coupled reproducibility issues for also known as PICM, with good mechanical strength. each oligomer made with hydrogenated MDI (HMDI They are resistant to abrasion and this isocyanate. The or H12MDI), saturated hydrolysis and retain gloss and reproducibility issues for MDI (SMDI), reduced MDI physical properties upon each oligomer may then (RMDI), and weathering. A unique feature of lead to unexpected dicyclohexylmethane *Desmodur ® W diisocyanate is its performance properties of diisocyanate ability to form optically clear formulated coating polyurethanes when combined with suitable polyol coreactants. *trademark of Bayer **definitions for abbreviations are as follows: TDI is toluene diisocyanate MDI is methylenebis(phenyl isocyanate) OR Methyl Di-P-Phenylene Isocyanate IPDI is isophorone diisocyanate HDI is Hexamethylene diisocyanate TMDI is Trimethyl hexamethylene diisocyanate TMXDI is TMXDI ® (Meta) Aliphatic Isocyanate, available from Cytec Industries Inc.

TABLE 1D Choice of Oligomer for Supercoatings-Primary Disadvantages-includes Selection of Inhibitor to Sub-Chemistry, within the undesirable interactions formulate oligomer category Benefits with other components 1. Hydroquinone type Hydroquinone, Methylether Improve process and shelf stability Color change; retard hydroquinone, Butyl polymerization reaction hydroxytoluene. 2. Butylated hydroxyl Phenolic Low Cost, good solubility, Less effective at higher toluene (most widely used) effective temperatures 3. Phenothiazine Improve Process and shelf stability Color change; retard polymerization reaction

TABLE 1E Choice of Oligomer for Supercoatings-Primary Disadvantages-includes Selection of Catalyst to Sub-Chemistry, within the undesirable interactions formulate oligomer category Benefits with other components 1. Amine compounds Tertiary amines Versatile catalyst Side reactions lead to byproducts, such as urea, isocyanate trimers. 2. Organometallic Mercury, lead, tin, bismuth, Highly effective Some are highly toxic and complexes zinc compounds hazardous

TABLE 2A Choice of Oligomer for Supercoatings-Secondary Disadvantages-includes Sub-Chemistry, within the undesirable interactions Chemistry of Oligomer category Benefits with other components 1. urethane (meth)acrylate other UV-curable end-groups fast cure, toughness, stability, high viscosity e.g. vinyl ether, versatility, many polyols available, (meth)acrylamide, vinyl amide ease of manufacture (most commonly used oligomer chemistry for optical fiber coatings) 2. polyester (meth)acrylate other UV-curable end-groups fast cure, low viscosity, versatility, low elongation, poorer e.g. vinyl ether, many polyols and acids available, hydrolytic stability, more (meth)acrylamide, vinyl amide oxidative stability difficult to manufacture 3. silicone (meth)acrylate other UV-curable end-groups hydrophobic and lipophobic, fast generally low Tg, e.g. vinyl ether, cure, stability, low viscosity expensive, specialized (meth)acrylamide, vinyl amide manufacture, refractive (diphenyl silicone acrylates index may be too low have high Tg) 4. hydrocarbon other UV-curable end-groups hydrophobic, hydrolytic stability, poorer oxidative stability, (meth)acrylate e.g. vinyl ether, low viscosity poorer solubility, (meth)acrylamide, vinyl amide lipophilic, generally low (aromatic and cyclic Tg hydrocarbons can have high Tg) 5. fluorocarbon other UV-curable end-groups hydrophobic and lipophobic, fast expensive, poorer (meth)acrylate e.g. vinyl ether, cure, stability, low viscosity solubility, refractive index (meth)acrylamide, vinyl amide may be too low, (aromatic and cyclic specialized manufacture, fluorocarbons can have high generally low Tg Tg) 6. acrylated acrylic polymer Other UV-curable end-groups Adjustable Tg, good stability, Specialized manufacture, or copolymer e.g. vinyl ether, good chemical resistance generally high viscosity (meth)acrylamide, vinyl amide 7. thiol-ene various enes including, strong network structure, low odor, shelf stability norbornene, vinyl ether, vinyl viscosity, good cured stability ester, vinyl amide, allyl ether, allyl ester, allyl amide, styrene, alkenes (aromatic or cyclic enes for higher Tg) 8. cationic epoxy various cationically curable low shrinkage, good adhesion, slower cure speed, post groups including glycidyl low viscosity, stability curing effect, lower ether, glycidyl ester, vinyl elongation ether, oxetane, hydroxyl (aromatic materials for higher Tg)

TABLE 2B Choice of Oligomer for Supercoatings-Secondary Chemistry of polyol to Disadvantages-includes formulate Urethane Sub-Chemistry, within the undesirable interactions with oligomer category Benefits other components 1. polyether (most poly(alkylene glycols), hydrolytic stability, flexibility, oxidative stability, generally commonly used polyol for poly(arylene glycols), cure speed, low viscosity low Tg optical fiber oligomers) copolymers with other types of polyols 2. polyester aliphatic, aromatic, linear, oxidative stability, higher Tg poorer oxidative stability branched 3. polycarbonate aliphatic, aromatic, linear, oxidative and hydrolytic stability, potential crystallinity branched higher Tg 4. hydrocarbon aliphatic, aromatic, linear, hydrophobic, good stability poor oxidative stability if branched, cyclic, saturated, unsaturated, solubility, unsaturated (aromatic and lipophilic cyclic hydrocarbons can have high Tg) 5. silicone aliphatic, aromatic, linear, hydrophobic and lipophobic, expensive, refractive index branched (diphenyl silicone stability, low viscosity may be too low, generally low acrylates have high Tg) Tg 6. bio-based Various vegetable, seed, nut, Generally low Tg, hydrophobic, May have lower purity or biomass and other plant- good stability, sustainable homogeneity derived polyols

TABLE 2C Choice of Oligomer for Supercoatings-Secondary Chemistry of Isocyanate to Disadvantages-includes formulate Urethane Sub-Chemistry, within the undesirable interactions with other oligomer category Benefits components 1. aromatic TDI, MDI faster reaction, low cost yellowing, toxicity 2. aliphatic IPDI, HDI, TMDI low yellowing higher cost, slower reaction 3. alkyl-aryl TMXDI stability higher cost, slower reaction

TABLE 2D Choice of Oligomer for Supercoatings-Secondary Chemistry of Inhibitor to Sub-Chemistry, within the Disadvantages-includes undesirable formulate oligomer category Benefits interactions with other components 1. Hydroquinone type Hydroquinone, Methylether Improve process and shelf Color change; retard polymerization hydroquinone, Butyl stability reaction hydroxytoluene. 2. Butylated hydroxyl Phenolic Low Cost, good Less effective at higher temperatures toluene (most widely used) solubility, effective 3. phenothiazine Improve process and shelf Color change, retard polymerization stability reaction

TABLE 2E Choice of Oligomer for Supercoatings-Secondary Chemistry of Catalyst to Sub-Chemistry, within the Disadvantages-includes undesirable formulate urethane oligomer category Benefits interactions with other components 1. Amine Compounds Tertiary amines Versatile catalyst Side reactions lead to byproducts, such as urea, isocyanate trimers. 2. Organometallic Mercury, lead, tin, bismuth, Highly effective Some are highly toxic and hazardous complexes zinc compounds

TABLE 1F Choice of Photoinitiator for Supercoatings-Primary Disadvantages-includes undesirable interactions Chemistry Benefits with other components 1. α-hydroxy ketones fast cure, low yellowing, low cost, good can be volatile through-cure and surface cure 2. (bis) acylphosphine oxides very fast cure, low yellowing, good more expensive, may have crystals through-cure 3. benzophenones low cost, good surface-cure require an amine, slower, yellows 4. polymeric photoinitiators low volatility, good through-cure and more expensive surface-cure 5. others (many) may have low cost generally slower-curing, may have lower shelf- stability, may yellow

TABLE 2F Choice of Photoinitiator for Supercoatings-Secondary Disadvantages-includes undesirable interactions Chemistry Benefits with other components 1. α-hydroxy ketones fast cure, low yellowing, low cost, good can be volatile through-cure and surface cure 2. (bis) acylphosphine oxides very fast cure, low yellowing, good more expensive, may have crystals, poorer through-cure, good for colored secondaries surface-cure 3. benzophenones low cost, good surface-cure require an amine, slower, yellows 4. polymeric photoinitiators low volatility, good through-cure and more expensive surface-cure 5. morpholino-containing good for colored secondaries may screen too much UV light from reaching primary coating in wet-on-wet process 6. others (many) may have low cost generally slower-curing, may have lower shelf- stability, may yellow

TABLE 1G Choice of Adhesion Promoter for Supercoatings-Primary Disadvantages-includes undesirable interactions Chemistry Benefits with other components 1. silane coupling agents good dry and wet adhesion moisture-sensitive (shelf-stability issue), possible to cause reduced cure speed and lower modulus 2. acid-functional materials good dry adhesion generally poorer wet adhesion 3. polar monomers or oligomers good dry adhesion generally poorer wet adhesion

TABLE 2G Choice of Adhesion Promoter for Supercoatings-Secondary Chemistry None, adhesion promoters are not used in Secondary Coatings, only in Primary Coatings

TABLE 1H Choice of Diluent Monomer for Supercoatings-Primary Disadvantages-includes undesirable interactions Chemistry Benefits with other components 1. alkyl (meth)acrylate generally low Tg, hydrophobic, good odor, slower cure speed, may be crystalline, stability, low cost, good diluent (generally volatile under high heat output of conventional monofunctional monomer used for lower mercury UV lights crosslink density and modulus) 2. aryl or cyclic (meth)acrylate generally higher Tg, hydrophobic may be volatile or crystalline 3. ether (meth)acrylate generally low Tg, fast cure speed, generally more hydrophilic, poorer oxidative stability good diluent, aromatics have good dry adhesion (generally monofunctional monomer used for lower crosslink density and modulus) 4. hydroxyl-functional, acid- good dry adhesion, fast cure speed generally higher Tg, more hydrophilic, can react functional, and other polar (generally monofunctional monomer used with other coating components monomers for lower crosslink density and modulus) 5. (meth)acrylamides and vinyl good dry adhesion, fast cure speed generally higher Tg, more hydrophilic amides (generally monofunctional monomer used for lower crosslink density and modulus)

TABLE 2H Choice of Diluent Monomer for Supercoatings-Secondary Disadvantages-includes undesirable interactions Chemistry Benefits with other components 1. alkyl (meth)acrylate hydrophobic, good stress-relaxation if volatility, odor, slower cure speed, may be branched, good stability, low cost, good crystalline diluent (generally multifunctional monomer used for higher crosslink density and modulus) 2. aryl or cyclic (meth)acrylate generally higher Tg, hydrophobic Some aryl species, e.g. phenoxy ethyl (generally multifunctional monomer used acrylate, are volatile under high heat output for higher crosslink density and modulus) of conventional mercury UV lights or crystalline; therefore when an aryl reactive diluent monomer is present that has a molecular weight less than about 300, it should be present at no more than about 10 wt. % of the total formulation 3. ether (meth)acrylate good stress-relaxation if branched, fast cure more hydrophilic, poorer oxidative stability speed, generally good diluent (generally multifunctional monomer used for higher crosslink density and modulus) 4. hydroxyl-functional, acid- fast cure speed more hydrophilic, can react with other coating functional, and other polar (generally multifunctional monomer used components monomers for higher crosslink density and modulus) 5. (meth)acrylamides and vinyl fast cure speed more hydrophilic amides (generally multifunctional monomer used for higher crosslink density and modulus)

TABLE 1J Choice of Stabilizer for Supercoatings-Primary Disadvantages-includes undesirable interactions Chemistry Benefits with other components 1. hindered phenol good for oxidative stability, low yellowing may have poor solubility, crystallinity, high cost 2. hindered amine good for low yellowing basicity (may lower glass strength), may react with other coating components 3. UV absorbers good for low yellowing may slow cure speed of both secondary and primary coating 4. others e.g. phosphites, may improve cured coating stability and may have poor solubility, crystallinity, high cost sulfides, metallic, mixed reduce yellowing stabilizers . . .

TABLE 2J Choice of Antioxidant for Supercoatings-Secondary Disadvantages-includes undesirable interactions Chemistry Benefits with other components 1. hindered phenol good for oxidative stability, low yellowing may have poor solubility, crystallinity, high cost 2. hindered amine good for low yellowing basicity (may lower glass strength), may react with other coating components 3. UV absorbers good for low yellowing may slow cure speed of both secondary and primary coating 4. others e.g. phosphites, may improve cured coating stability and may have poor solubility, crystallinity, high cost sulfides, metallic, mixed reduce yellowing stabilizers . . .

In contrast to the “two-dimensional” approach illustrated in FIG. 1, FIG. 2 illustrates step 2 is the first aspect of the instant claimed invention method for formulating Supercoatings for Optical Fiber. FIG. 2 shows six Decision Charts, 10, 20, 30, 40, 50 and 60 linked together in a three dimensional model by linking lace 307. Linking Lace 307 illustrates that any formulation change made in either the Primary Coating Layer or the Secondary Coating Layer of an Optical Fiber Supercoatings means that the other desired properties of an Optical Fiber Supercoatings must be tested after the initial change has been made, in order to be certain that one or more changes in the formulation don't lead to a negative influence on one or more functional properties of the Primary Coating Layer and Secondary Coating Layer.

The six necessary properties for Supercoatings for Optical Fiber are as follows:

The cured Primary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity:

A) a % RAU of from about 84% to about 99%;

B) an in-situ modulus of between about 0.15 MPa and about 0.60 MPa; and

C) a Tube Tg, of from about −25° C. to about −55° C.;

wherein the cured Secondary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity:

A) a % RAU of from about 80% to about 98%;

B) an in-situ modulus of between about 0.60 GPa and about 1.90 GPa; and

C) a Tube Tg, of from about 50° C. to about 80° C.

Step ii) of the instant claimed invention, as illustrated in FIG. 2, shows that any formulation change made to affect one of these six properties, means that all of the other five functional properties must be tested as well, to make sure that changing one aspect of the Supercoatings does not affect the other five aspects.

FIG. 3 shows the second embodiment of step ii) of the instant claimed method for formulating Supercoatings for Optical Fiber. In FIG. 3, the possible changes involving reformulation of a Primary Coating Layer or Secondary Coating Layer of Supercoatings must be tested against each other to see if one change to achieve a desired functional property could also cause other changes that would negate a desired functional property.

FIG. 4 shows the third embodiment of step ii) of the instant claimed method for formulating Supercoatings for Optical Fiber. In FIG. 4, the possible changes are linked by linking laces both horizontally and vertically amongst the six necessary functional Supercoatings properties. This linkage of properties is the essence of what makes Supercoatings for Optical Fibers different from simply a primary coating covered by a secondary coating layer. With Supercoatings for optical fiber, the reality is that instead of formulating the Primary and Secondary coating layers separately from each other, that any formulation change in one of the layers, must be tested against all the properties required of the Supercoatings.

The second aspect of the instant claimed invention is the Method of the first aspect of the instant claimed invention, in which the Three-Dimensional Laced Methodology includes using a Multi-Layer Film Drawdown method to evaluate composite fused Primary Coating Layer and Secondary Coating Layer of Radiation curable Supercoatings.

The third aspect of the instant claimed invention is a Multi-Layer Film Drawdown Method comprising the steps of:

-   -   a) selecting a substrate for the test;     -   b) applying a Primary coating to the substrate using a defined         thickness drawdown bar;     -   c) optionally curing the Primary coating;     -   d) applying a Secondary coating to the Primary coating using a         defined thickness drawdown bar, wherein the defined thickness of         the drawdown bar to apply the Secondary coating is greater than         the defined thickness of the drawdown bar used to apply the         primary coating;     -   e) applying radiation to the multi-layer film sufficient to         effectuate the cure of both the Primary and Secondary into a         Fused Composite film;     -   f) removing the film from the substrate; and         -   evaluating the functional properties of the cured film.

FIG. 5 shows one such Film.

The Multi-Layer Film Drawdown method flat plate substrate method for evaluation of layers of potential Radiation curable Supercoatings-Primary and Secondary Layers comprises the following steps:

1) For reference the general method for preparing drawdown films for UV curing is described by Szum et al., 43rd IWCS Proceedings (1994), p. 59.

2) The typical practice is to start with a clean single-thickness window-pane glass. One or more small daubs of test coatings are applied to the glass plate itself, or to an overlaid polyester sheet covering the glass plate, and drawn down with a Bird type calibrated bar to spread a coherent thin film of 25p to 75p. One such Bird type bar for the first layer has a film deposit height of 1.5 mils. These test coatings are most typically inner primary coatings.

3) Immediately after this first drawdown, a second drawdown is made over the top and wide enough to cover the edges of the first drawdown films. This second drawdown is also made with a Bird type bar calibrated to deposit a film of typically 75μ to 254μ. One such Bird type bar for the second layer has a film deposit height of 3.0 mils. The glass plate with the two drawdowns and the consequent composite films is exposed to suitable actinic radiation to achieve the desired degree of cure. This method is known as the wet-on-wet method.

4) A similar method known as wet-on-dry method, is conducted in the same manner as the wet-on-wet method described above; except the first drawdown films are exposed to actinic radiation to effectuate the cure of the Primary Coating Layer. After this radiant exposure the second drawdown is made and the plate is then further exposed to radiation to effectuate the cure of the Secondary Layer and the Primary Layer into a Fused Composite film.

5) This procedure results in the glass plate having upon its surface area cured composite films composed of a first layer of specified thickness and a second layer of a thickness calculated by the difference of the thickness of the first layer subtracted from the nominal thickness of the calibrated Bird type bar used for the second overcoating drawdown. These Fused Composite films are then suitable for typical testing related to the properties desirable in Radiation curable Supercoatings intended for optical fiber applications.

The method is used to apply some small dots of primary to a glass plate and drawdown with a 1 mil or 1.5 mil Bird Bar. While the primary is still uncured, a second drawdown of a colored secondary coating layer is made over the primary coating layer but with a 3 mil bar. The result is observed to be acceptably uniform as can be seen in FIG. 5.

In practice, the Supercoatings Primary Layer is drawn down with a 1.5 mil bar, then a candidate for Supercoatings Secondary layer, observed as a brown layer, Example 3SA3 Color twoH, (Color 2HBrown) is drawn down over the Supercoatings Primary with a 3 mil bar. After this wet-on-wet application, the plate is exposed to radiation sufficient to effectuate the cure of both the Primary Coating Layer and the Secondary Coating Layer into a Fused Composite Film.

In FIG. 5, The Fused Composite film appears to be very uniform with the darker areas being 3 mil of colored secondary, and the lighter areas 1.5 mil each of primary and colored secondary over the top. The Fused Composite film is easily removable and hand able for measurements of thickness and % RAUs, a critical measurement for both layers of Supercoatings for Optical Fiber.

Follow-up analysis shows very little mixing of the layers during the dual-drawdown method.

It was surprising to discover that a simple w-o-w drawdown would leave both the bottom and top layers intact with their separate identities, and yet the two layers then fuse into a Fused Composite film during cure.

The lack of mixing of the layers is further illustrated in FIGS. 7, 8 and 9.

FIG. 7 is Spectra “all”, which shows 4 spectra with a comparable appearance to two sets of two sitting on top of each other.

FIG. 8 is Spectra “Brown” showing the colored secondary portion only, and the top of the dual drawdown portion. The two spectra match up quite well.

FIG. 9 is Spectra “formulation Option A for the Supercoatings Primary Layer from Example 3SA3 Color twoH, (Color 2HBrown)” showing the glass side of the dual layer, and the glass side of a single 3 mil Example 3 Supercoatings Primary Layer drawdown. Again the spectra match up very well.

These composite films are then suitable for typical testing related to the properties desirable in Radiation curable Supercoatings intended for optical fiber applications. Testing can include % RAU. This is especially of value when the Secondary layer is being applied wet over a wet Primary Coating Layer and it becomes critical that the cure rate of the Secondary layer is not faster than the cure rate of the Primary Coating layer because if the Secondary Coating cures faster than the primary coating then the Primary Coating may never cure to its desired % RAU because the optical transmission of cured Secondary Coating Layer is typically less than that of liquid, uncured Secondary Coating Layer.

An interesting observation is that with this new Method of Formulating Radiation curable Supercoatings for Optical Fiber it has been possible to formulate Radiation curable Supercoatings with the following enhanced functional Properties:

A % RAU that ranges now to an upper limit of about 100% for both the Primary Coating Layer and the Secondary Coating Layer.

This method permits the investigation of the properties of primary and secondary as a composite Supercoatings film in ways not available in the past. With this method it is now possible to conduct feasibility studies of Supercoatings Candidate Secondary Layers over Supercoatings Candidate Primary Layers for tensile properties, DMA characteristics, environmental durability, etc., with easily handled films instead of having to use the Draw Tower Simulator. There are many understood benefits of using the Multi-layer Film Drawdown method, including, but not limited to the following: the film drawdown takes away the line speed as a factor in coatings functionality to allow for more basic analysis; it also allows the formulator to evaluate the migration of materials from layer to layer during the wet on dry and wet on wet processing steps.

Another advantage of the Multi-Layer Film Drawdown method is that it is critical for both wet on wet processing and wet on dry processing that sufficient through cure is possible to cure the primary coating to the requisite percentage RAU when the coating is applied to wire or optical fiber. In practice, it is known that in Wet on dry processing, the primary coating may be undercured to achieve line speed with the expectations that the cure will be finished in the primary coating when the radiation is applied to the secondary coating. Therefore use of the Multi-Layer Film Drawdown method is helpful to simulate wet on wet application as compared to wet on dry application and testing the % RAU to determination of cure of primary through the secondary. The simulation allows the formulator to quickly evaluate the efficacy of different photoinitiators. This testing has already led to the hypothesis that for Radiation Curable Supercoatings for Optical Fiber, to achieve the very high levels of % RAU that are desired and required, it is believed, without intending to be bound thereby, to be better to have a different chemical type of photoinitiator in the Secondary Coating layer than in the Primary Coating layer.

In this way, there will be two different photo initiated reactions taking place in the layers, rather than having one photoinitiator try to achieve the desired level of cure in both layers.

Another benefit of the Multi-layer film drawdown method is approximating the composite behavior of the cured secondary coating layer over the cured primary coating that can be correlated with Primary and Secondary characteristics that can be defined in SUPERCOATINGS. It is possible to evaluate the functional properties of each coating layer by analyzing film using solid film theology testing, otherwise known as DMA (dynamic Mechanical Analysis)

The conclusion is that there is very little intermixing during the dual drawdown process, and that the method is useful in evaluating candidates for Supercoatings Primary Coating Layers and Supercoatings Secondary Coating Layers.

The following examples further illustrate the invention but, of course, should not be construed as in any way limiting its scope.

EXAMPLES

The ingredients listed in these Examples have the following commercial names, are available from the listed source and have the indicated chemical composition.

Commercial Name Supplier Description Ebecryl 3700 Cytec Bisphenol A diglycidylether diacrylate Celloxide 2021P Daicel Chemical Cycloaliphatic epoxy Eponex 1510 Hexion Hydrogenated bisphenol A diglycidylether OXT-101 Toagosei 3-ethyl-3-hydroxymethyl-oxetane SR 492 Sartomer Propoxylated trimethylolpropane triacrylate Pluracol GP430 BASF Propoxylated glycerol (polyether triol) Silwet L-7600 Momentive Polyalkyleneoxide modified polydimethylsiloxane BYK-A-501 BYK-Chemie silicone-free solution of foam destroying polymers Irganox 1035 Ciba Hindered phenol antioxidant PRINT Blue 15DT7083 The Flint Group Phthalocyanine Blue pigment Hostaperm Violet RL, Clariant Carbozole Violet pigment Pigment Violet 23 IRGACURE 184 Ciba 1-hydroxycyclohexyl phenyl ketone, free radical photoinitiator Chivacure-1176 Chitec mixture of triarylsulfonium hexafluoroantimonate salts, cationic photoinitiator BR-543 Bomar Specialties Aliphatic urethane diacrylate oligomer SR 344 Sartomer Polyethylene glycol (400) diacrylate (MW 508) SR 504D Sartomer Ethoxylated(4) Nonylphenol acrylate (MW 450) SR 531 Sartomer Cyclic trimethylolpropane formal acrylate (MW 200) SR 395 Sartomer Isodecyl acrylate (MW 192) Irgacure 651 Ciba α,α-dimethoxy-alpha-phenylacetophenone free radical photoinitiator Vinyl Caprolactam BASF Vinyl amide

Abbreviation Meaning BHT 2,6-di-tert-butyl-4-methylphenol, available from Fitz Chem. CN-120Z epoxy diacrylate, available from Sartomer. DABCO 1,4-diazabicyclo[2.2.2]octane, available from Air Products. DBTDL dibutyl tin dilaurate, available from OMG Americas. HEA hydroxyethyl acrylate, available from BASF HHPA hexahydrophthalic anhydride, available from Milliken Chemical. SR-506 isobornyl Acrylate, available as from Sartomer. Photomer 4066 ethoxylated nonylphenol acrylate, available from Cognis. Pluracol 1010 polypropylene glycol (MW = 1000), available from BASF; SR-306HP tripropylene glycol diacrylate (TPGDA), available from Sartomer. SR-349 ethoxylated bisphenol A diacrylate, available from Sartomer. Mondur ® TDS Grade II Monomeric toluene diisocyanate (TDI); a high 2,4-isomer TDI; NCO weight 48%, viscosity 3 mPa · s@25° C., equivalent weight 87.5; functionality 2; available from Bayer TDI An 80/20 blend of the 2,4- and 2,6-isomer of toluene diisocyanate, available from BASF IPDI Isophorone diisocyanate, available from Bayer TPO 2,4,6-trimethylbenzoyldiphenylphosphine oxide type photoinitiator, available from Chitech.

The present invention is further illustrated with a number of examples.

In all of these examples, the process is as follows:

-   -   Step One: determining the maximum Acceptable Increase in         Attenuation requirements for the telecommunications network         where the optical fiber will be installed;     -   Step Two: determining the Field Application Environment of the         Supercoatings by understanding the:         -   i) type of glass being used in the optical fiber;         -   ii) whether the Supercoatings Secondary Layer will be             applied over the Supercoatings Primary Layer wet on dry or             wet on wet;         -   iii) the type, number of lights and positioning of lights             along the draw tower manufacturing line that are used to             cure the Supercoatings on the optical fiber; and         -   iv) the line speed at which the Supercoatings will be             applied;     -   Step Three: using a Three-Dimensional Laced Methodology of         -   i) Evaluation of candidate Radiation curable Supercoatings             by evaluation of the Radiation curable Supercoatings Primary             Layer and Secondary Layer for the Six defined Radiation             curable Supercoatings parameters;         -   ii) Testing the Radiation curable Supercoatings Primary             Layer and the Secondary Layer to determine if the required             functional property(s) of Supercoatings are achieved;             -   wherein if the required functional property of                 Supercoatings has not been achieved, reformulating             -   either or both of the Primary or Secondary coating;         -   iii) testing the reformulated Primary or Secondary Coating             to determine if the desired functional property is achieved;             -   wherein if the desired functional property is achieved                 then proceeding to step d);             -   wherein if the desired functional property is not                 achieved, then repeat steps ii) and iii) until the             -   desired functional property is achieved; and then     -   Step Four: integrating the effects of reformulation of the         Supercoatings Primary Coating Layer and the Supercoatings         Secondary Coating Layer by evaluating the change in the         formulation relative to all the other defined functional         property requirements of Supercoatings; and     -   Step Five: using the results from the Three-Dimensional Laced         Methodology to finalize the selection of Supercoatings to         provide the properties required to achieve the Maximum         Acceptable Increase in Attenuation of the coated optical fiber.

Example 1 Request for Supercoatiags for Microbeading Resistant Single Mode Optical Fiber

An optical fiber manufacturer wishes to apply a radiation curable Supercoatings to their Single Mode Optical Fiber.

The glass used in this Single Mode Optical Fiber is of the most modern type, able to resist Microbending.

Step One:

The requested Microbending Sensitivity for optical fiber used in this network is reported at:

dB/Km of less than about 0.06 at 1310 nm and −60° C.;

dB/Km of less than about 0.11 at 1550 nm and −60° C.; and

dB/Km of less than about 0.15 at 1625 nm and −60° C.

Step Two

Commercial Fiber Data

The radiation curable Radiation curable Supercoatings is applied Wet on Dry.

The curing lights available are: 600w/10 inch D Lamps.

The number of curing lights are: 2 in the primary area and 4 after the secondary coating is applied-possibly up to 5 if needed.

The line speed at which the Supercoatings will be applied is about 1400 m/minute.

Step Three-Formulating Supercoatings

Four different formulators are given the task of working on potential Primary Coating Layers for this radiation curable Supercoatings.

Each Primary Coating Formulator selects the raw materials for their starting Oligomer, then the photoinitiator(s), antioxidant, one or more diluent monomers and other additives based on information available. In general, without intending to be bound thereby, the oligomer synthesis is carried out as follows:

Oligomers suitable for coating compositions of the invention are prepared by reaction of at least one polyether polyol, at least one diisocyanate, at least one hydroxyl terminated acrylate or (meth)acrylate, and optionally an alcohol. The following oligomer synthesis methods illustrate two different methods for synthesizing the oligomer. However, it will be appreciated by the skilled artisan that other synthesis methods also can be used so long as the oligomer comprises a urethane-backbone, with at least one terminal unsaturated group such as an alkenyl group or vinyl group.

Oligomer Synthesis—Method A is also known as an “outside-in” method that first reacts the isocyanate with hydroxyl terminated acrylate or methacrylate, followed by the reaction with polyol.

To a mixture of diisocyanate and inhibitor, HEA is added in a controlled manner so that the temperature does not exceed 40° C. The mixture is allowed to react at 40° C. for 2 h so that the desired NCO content is reached. Polyol and catalyst are then added, and the mixture is allowed to react at 80° C. for 2 h or longer, until the NCO content is not greater than 0.10.

Oligomer Synthesis—Method B is also known as an “inside-out” method that first reacts the isocyanate with polyol, followed by the reaction with hydroxyl terminated acrylate or methacrylate.

Catalyst is added to a mixture of diisocyanate, polyol and inhibitor. The mixture is allowed to react at 60° C. for 2 h, so that the desired NCO content is reached. Then, HEA is added, and the mixture is allowed to react at 85° C. for 1 h or longer, until the NCO content is not greater than 0.05.

Polyether polyols suitable for preparing oligomers in accordance with the invention preferably are selected from the group consisting of a polyethylene glycol and a polypropylene glycol. In an embodiment, the polyether polyol is a polypropylene glycol.

Catalysts for synthesizing urethane based oligomers for use in radiation curable coatings for optical fiber are known in the art. The catalyst is selected from the group consisting of copper naphthenate, cobalt naphthenate, zinc naphthenate, triethylamine, triethylenediamine, 2-methyltriethyleneamine, dibutyl tin dilaurate (DBTDL); metal carboxylates, including, but not limited to: organobismuth catalysts such as bismuth neodecanoate, CAS 34364-26-6; zinc neodecanoete, CAS 27253-29-8; zirconium neodecanoate, CAS 39049-04-2; and zinc 2-ethylhexanoate, CAS 136.53-8; sulfonic acids, including but not limited to dodecylbenzene sulfonic acid, CAS 27176-87-0; and methane sulfonic acid, CAS 75-75-2; amino or organo-base catalysts, including, but not limited to: 1,2-dimethylimidazole, CAS 1739-84-0; and diazabicyclo[2.2.2]octane (DABCO), CAS 280-57-9 (strong base); and triphenyl phosphine; alkoxides of zirconium and titanium, including, but not limited to zirconium butoxide, (tetrabutyl zirconate) CAS 1071-76-7; and titanium butoxide, (tetrabutyl titanate) CAS 5593-70-4; and ionic liquid phosphonium, imidazolium, and pyridinium salts, such as, but not limited to, trihexyl(tetradecyl)phosphonium hexafluorophosphate, CAS No. 374683-44-0; 1-butyl-3-methylimidazolium acetate, CAS No. 284049-75-8; and N-butyl-4-methylpyridinium chloride, CAS No. 125652-55-3; and tetradecyl(trihexyl) phosphonium.

All of these catalysts are commercially available.

In an embodiment, the catalyst is DBTDL or is an organobismuth catalyst such as “COSCAT 83” proprietary organobismuth catalyst, available from CosChem.

The choice of Photoinitiator is determined by:

-   -   1) the radiation source, intensity, proximity to the coating     -   2) the coating layer thickness,     -   3) whether the formulation is clear or whether the formulation         contains pigments, and if “pigment-containing” the type of         pigment and the amount of pigment present in the formulation.     -   4) the types of oligomers present in the composition     -   5) whether the coating composition is the Primary or Secondary         coating layer, and whether the Secondary Coating Layer is         applied wet-on-wet or wet-on-dry.

There are two general classes of photoinitiators:

Type I: photoinitiators undergo a uni-molecular bond cleavage upon irradiation to yield free radicals Type II: photoinitiators undergo a bimolecular reaction where the excited state of the photoinitiator interacts with a second molecule (a co-initiator) to generate free radicals.

UV photoinitiators of both Type I and Type II are available.

Two different formulators are given the task of working on potential Secondary Coating Layers for this radiation curable Supercoatings.

Each Secondary Coating Formulator selects the raw materials for their starting Oligomer, then the photoinitiator(s), antioxidant, one or more diluent monomers and other additives based on information available.

In selecting their raw materials, each Secondary Coating Formulator takes into account the following: TDI Type II is inexpensive, and is a fast reacting isocyanate. Further to the selection of TDI Type II for use in Secondary Coatings, group contribution theory (takes the characteristics of each part of the group and contributes) teaches that the aromatic group in the isocyanate contributes to high Tg and high modulus in the secondary, which is a technical reason why aromatic isocyanates would be favored for secondary coatings.

BHT Food Grade: Antioxidant scavenges free radicals (which is important because HEA (inhibited by methyl hydroquinone) can self-polymerize); therefore a synthetic chemist plans the synthesis to have the BHT in the reaction mixture before the HEA The scavenging reaction also requires the presence of oxygen-it is known that the oxygen in normal ambient air is typically sufficient for this purpose.

2-HEA (2-hydroxy ethyl acrylate) is a simple acrylate which historically has yielded very good cure rates in formulated radiation curable coatings for optical fiber. HBA (hydroxy butyl acrylate) or HPA (hydroxyl ethyl acrylate) are known to be not as reactive in the synthesis.

Both the Primary Coating Formulators and the Secondary Coating Formulators are aware of the following as they formulate; the polymerization of the secondary coating layer causes shrinkage of that layer and the shrinkage of the secondary coating layer puts pressure on the primary coating layer, whether the primary coating layer is already cured or is in the process of being cured when the secondary coating layer is being cured. Stress relaxation is a measure of the relief of stress on the primary caused by the shrinkage of the secondary coating as the secondary coating polymerizes. The temperature of the polymerization of the Secondary Coating Layer of a Supercoating has to be above the Tg for fast relief of that shrinkage. In formulating radiation Curable Supercoatings for Optical Fiber, it is assumed that the temperature of the polymerization of both the Primary and Secondary coating layer is well above their Tg's. If the polymerization temperature is below Tg, the stress relaxation is not as fast. If stress relaxation does not timely occur, the stress on the optical fiber can lead to unacceptable attenuation.

Wet on Wet processing has the potential for additional stress relaxation issues only because the fiber is being coated with two liquids before any polymerization occurs and both liquids are potentially cooler than the fiber, then there will be simultaneous polymerization taking place with dual heats of polymerization so as the curing takes place the temperature profile is uneven between the coating layers. Again, the formulators have to be aware of the fact that with the polymerization taking place simultaneously the difference in cross-link density is also a huge factor as there is much less cross-link-density in the primary coating as there is the secondary.

In the field of optical fiber manufacture it is known that the fiber cabler desires that the optical fiber is in a relaxed state before the optical fiber is manipulated further during the cabling process.

Thus, all formulators have to be aware that minimizing stress relaxation issues is critical, otherwise, the cabling operation will take longer as the cabler has to wait longer after the coatings are applied to the optical fiber to cable the optical fiber to allow for more stress relaxation to occur. It is known if the formulators misformulate such that the primary coating layer and the secondary coating layer don't relax properly and timely, it will be very, very difficult for the cabled optical fiber to not exceed the you never achieve the Maximum Acceptable lucrease in Attenuation.

To enhance stress relaxation the formulators select materials that are more flexible in the secondary coating; however, these flexible materials must be selected in such a way that the additional flexibility does not negatively interfere with targeted physical properties of high Tg and high strength.

Examples 1-4

These Examples illustrate Formulator Alpha's candidate formulations for the candidate Primary Coating Layer of the Supercoatings.

Example Example Example Example 1PA1 1PA2 1PA3 1PA4 Material Description wt. % wt. % wt. % wt. % Oligomer ACCLAIM polyol 4200 53.03 51.68 53.03 53.03 2,6-di-tert-butyl-p-cresol 0.09 0.09 0.09 0.09 IPDI 4.73 4.76 4.73 4.73 dibutyl tin dilaurate 0.03 0.03 0.0 0.03 zinc neodecanoate 0.0 0.0 0.03 0.0 dodecylbenzene sulfonic 0.0 0.0 0.00 0.0 acid 2-HEA 1.72 1.94 1.72 1.72 Total Oligomer wt. % 59.60 58.50 59.60 59.60 IRGACURE 819 1.50 1.50 1.50 2.00 IRGANOX 1035 0.60 0.60 0.60 0.60 TINUVIN 123 0.10 0.10 0.10 0.10 ethoxylated nonyl phenol 26.45 34.05 26.45 26.10 acrylate SR 349D Monomer 1.50 1.00 1.50 1.50 SR 339C (PEA) 9.00 3.00 9.00 9.00 THIOCURE TMPMP 0.75 0.75 0.75 0.6 A-189 0.50 0.50 0.50 0.50 Total (due to rounding of 100.00 100.00 100.00 100.00 significant figures may be +/−0.10 wt. %)

Examples 1PB1-1PB4

These Examples illustrate Formulator Beta's candidate formulations for the Primary Coating Layer of the Supercoatings

Example Example Example Example 1PB1 1PB2 1PB3 1B4 Material Description wt. % wt. % wt. % wt. % Oligomer ACCLAIM polyol 4200 45.78 45.78 45.78 45.78 acrylic acid, 99% 0.01 0.01 0.01 0.01 BHT 0.04 0.04 0.04 0.04 Mondur TDS Grade II 2.92 2.92 2.92 2.92 dibutyltin dilaurate 0.0 0.0 0.02 0.02 zinc neodecanoate 0.02 0.0 0.0 0.0 dodecylbenzene 0.0 0.02 0.0 0.0 sulfonic acid 2-HEA 1.24 1.24 1.24 1.24 Total Oligomer wt. % 50.01 50.01 50.01 50.01 IRGANOX 1035 0.50 0.50 0.50 0.50 SR-504D 46.29 46.29 46.29 46.29 SR 349D 0.91 0.91 0.91 0.91 TINUVIN 123 0.10 0.10 0.10 0.10 IRGACURE 819 1.20 1.20 1.20 0.0 TPO 0.0 0.0 0.0 1.20 A-189 0.99 0.99 0.99 0.99 Total (due to rounding of 100.00 100.00 100.00 100.00 significant figures may be +/−0.10 wt. %)

Examples 1PC1 Through 1PC4

These Examples illustrate Formulator Gamma's candidate formulations for the Primary Coating Layer of the Supercoatings.

Example Example Example Example 1PC1 1PC2 1PC3 1PC4 Material Description wt. % wt. % wt. % wt. % Oligomer ACCLAIM polyol 4200 57.47 57.44 57.44 57.18 BHT 0.1 0.1 0.1 0.1 IPDI 5.25 5.25 5.25 5.25 dibutyltin dilaurate 0.03 0.03 0.03 0.03 zinc neodecanoate 0.0 0.03 0.0 0.15 dodecylbenzene 0.0 0.0 0.03 0.15 sulfonic acid 2-HEA 2.15 2.15 2.15 2.14 Total Oligomer wt. % 65.00 65.00 65.00 65.00 SR-504D 21.55 21.55 21.55 21.55 SR 339C 9 9 9 9 SR 349D 1 1 1 1 IRGACURE 819 1.5 0.0 0.75 0.5 TPO 0.0 1.5 0.75 1.00 IRGANOX 1035 0.6 0.6 0.6 0.6 TINUVIN 123 0.1 0.1 0.1 0.1 A-189 1.25 1.25 1.25 1.25 Total (due to rounding of 100.00 100.00 100.00 100.00 significant figures may be +/−0.10 wt. %)

Examples 2SA1-2SA5 illustrate Formulator Episilon's candidate formulations for the Secondary Coating Layer

Ex. Ex. Ex. Ex. Ex. Secondary 2SA1 2SA2 2SA3 2SA4 2SA5 Material Description Wt. % Wt. % Wt. % Wt. % Wt. % Oligomer OligMT* 29.95 Oligomer OligTT** 29.95 28.78 29.95 Oligomer OligWT*** 29.95 Oligomer Wt. % of 29.95 29.95 29.95 28.78 29.95 total formula CN110 39.85 39.85 39.85 38.42 39.85 SR-506A 7.4 7.4 7.4 7.2 7.4 SR 339C(PEA) 8.4 8.4 8.4 8.15 8.4 SR 306F(TPGDA) 5.9 5.9 5.9 5.76 5.9 SR 238 MONOMER 4.5 4.5 4.5 4.27 4.5 CPI-6992 SARBOX SB520E35 2.43 TPO HP 1 1 1 Irgacure 819 1 0 1 1-Hydroxycyclohexyl- 2 2 2 3 2 Phenyl Ketone IRGANOX 1035 0.5 0.5 0.5 0.5 0.5 FF(W&C) DC-190 Surfactant 0.33 0.33 0.33 0.33 0.33 DC-57 Additive 0.17 0.17 0.17 0.17 0.17 Total (due to rounding of 100 100 100 100 100 significant figures may be +/−0.10 wt. %) *Oligomer **Oligomer ***Oligomer OligMT OligTT OligWT TDI Type II 22.47 21.26 22.32 BHT Food Grade 0.07 0.05 0.05 2-HEA 13.99 14.18 16.08 Dibutyltin Dilaurate 0.07 0.05 0.05 Pluracol P1010 63.41 64.46 61.50 Total (due to rounding of 100 100 100 significant figures may be +/−0.10 wt. %)

Examples 2SB1-2SB4

These Examples illustrate Formulator Zeta's Candidate formulations for the Secondary Coating Layer of the Supercoatings

Ex. Ex. Ex. Ex. Ex. Secondary 2SB1 2SB2 2SB3 2SB4 2SB5 Material description Wt. % Wt. % Wt. % Wt. % Wt. % Oligomer OligMT* 30.00 24.60 Oligomer OligTT** 30.00 27.80 Oligomer 30.00 OligWT*** Oligomer Wt. % of 30.00 24.60 30.00 27.80 30.00 total formula CN120Z 40.00 45.40 40.00 42.20 40.00 SR-506A 7.5 7.5 7.5 7.5 7.5 SR 339C 8.5 8.5 8.5 8.5 8.5 SR 306F 6 6 6 6 6 SR 238 4.5 4.5 4.5 4.5 4.5 Irganox 1035 FF 0.5 0.5 0.5 0.5 0.5 Irgacure 819 0.0 0.0 0.0 0.0 0.0 TPO HP 0.5 0.5 0.5 0.5 0.5 1- 2 2 2 2 2 Hydroxycyclohexyl- Phenyl Ketone DC-190 Surfactant 0.33 0.33 0.33 0.33 0.33 DC-57 Additive 0.17 0.17 0.17 0.17 0.17 Total (due to rounding of 100 100 100 100 100 significant figures may be +/−0.10 wt. %) *Oligomer **Oligomer ***Oligomer OligMT OligTT OligWT TDI Type II 22.47 21.26 22.32 BHT Food Grade 0.07 0.05 0.05 2-HEA 13.99 14.18 16.08 Dibutyltin Dilaurate 0.07 0.05 0.05 Pluracol P1010 63.41 64.46 61.50 Total (due to rounding of 100 100 100 significant figures may be +/−0.10 wt. %)

The results of the Multilayer Film Drawdown analysis show the most compatible potential combinations are:

1PA2 and 2SA4

1PA2 and 2SB3

1PB3 and 2SA4

1PB3 and 2SB3

1PC1 and 2SA4

1PC1 and 2SB3

1PD5 and 2SA4

1PD5 and 2SB3

These combinations are then run on the Draw Tower Simulator.

Certain combinations are found to achieve the properties of a Supercoating at some, but not all, of the line speeds between about 750 m/min and about 2,100 m/min

These combinations are found to be Supercoatings at all line speeds:

wherein the composition of the Primary Coating layer, prior to curing, is selected from the group

consisting of the formulations of Examples 1PA2, 1PB3, 1PC1; and

wherein the composition of the Secondary Coating layer, prior to curing, is selected from the group

consisting of the formulations of Examples 2SA4 and 2SB3.

Example 2

An optical fiber manufacturer wishes to save energy costs by switching at least part of their curing lights over to LED lights. They decide to start the switch by changing their lights curing the primary coating to LED lights. Their current primary coating is Example 1PB3 (from Example 1).

The Single Mode Optical Fiber is of the most modern type, able to resist Microbending.

Step One:

The requested Microbending Sensitivity for single mode optical fiber used in this network is reported at:

dB/Km of less than about 0.02 at 1310 nm and −60° C.;

dB/Km of less than about 0.03 at 1550 nm and −60° C.; and

dB/Km of less than about 0.05 at 1625 nm and −60° C.

Step Two

The Single Mode Optical Fiber is of the most modern type, able to resist Microbending

The radiation curable Radiation curable Supercoatings is applied Wet on Dry.

The type of curing lights for the primary coating are: The optical fiber manufacturer wants the flexibility of working with any LED lamp at 395 nm with a power of at least 4 W/cm².

For purposes of this Example, the LED Lamp chosen is a 8W/cm² LED unit with a peak emission at 395 nm. This type of LED lamp is available from Phoseon as an RX Fireline LED unit.

The number of curing lights are: from 1 to 3 in the Primary Coatings area,

The type of curing lights for the secondary coating are: 600w/10 inch D Lamps

The number of curing lights: 3 in the Secondary Coatings Area

The line speed at which the Supercoatings will be applied is approximately 1300 m/min.

Example Example 2Alpha 2Beta LED Curable LED Curable Version of Version of LED Curable Primary Coatings Example 1PB3 Example 1PB3 Components Description wt. % wt. % {circumflex over ( )}Acclaim PPG 4200/TDI/HEA urethane acrylate oligomer 47.56 47.05 Ethoxylated bisphenol A monomer 0.85 0.84 diacrylate Ethoxylated nonylphenol acrylate monomer 44.09 43.62 Lucirin TPO-L 2,4,6-trimethylbenzoyl ethoxy 5.00 5.00 phenyl phosphine oxide Irgacure 819 bis(2,4,6-trimethylbenzoyl)- 1.00 2.00 phenylphosphineoxide Irganox 1035 hindered phenol antioxidant 0.47 0.47 Bis-(1-octyloxy-2,2,6,6- 0.09 0.09 tetramethyl-4-piperidinyl) sebacate light stabilizer A-189 γ-mercaptopropyl trimethoxy 0.94 0.93 silane Total (due to rounding of 100.00 100.00 significant figures may be +/−0.10 wt. %)

Ingredients in {circumflex over ( )}Acclaim PPG 4200/TDI/HEA Oligomer Wt. % ACCLAIM polyol 4200 91.54 acrylic acid, 99% 0.02 BHT 0.08 Mondur TDS Grade II 5.83 dibutyltin dilaurate 0.05 2-HEA 2.48 Total (due to rounding of significant 100.00 figures may be +/−0.10 wt. %)

Therefore the fourth aspect of the instant claimed invention is a single-mode optical fiber coated with Supercoatings, wherein said Supercoatings comprise,

-   -   Primary Coating Layer and a Secondary Coating Layer,     -   wherein the composition of the Primary Coating layer, prior to         curing, is selected from the group consisting of the         formulations of Examples 1PA2, 1PB3, 1PC1, 2Alpha, 2Beta; and         wherein the composition of the Secondary Coating layer, prior to         curing, is selected from the group consisting of the         formulations of Examples 2SA4 and 2SB3 and 5SA1.

Example 3

An optical fiber manufacturer—wishes to apply a radiation curable Supercoatings for their Single Mode Optical Fiber. The Single Mode Optical Fiber is of the most modern type, able to resist Microbending.

Step One:

The requested Microbending Sensitivity for single mode optical fiber used in this network is reported at:

dB/Km of less than about 0.02 at 1310 nm and −60° C.;

dB/Km of less than about 0.06 at 1550 nm and −60° C.; and

dB/Km of less than about 0.09 at 1625 nm and −60° C.

Step Two

The Single Mode Optical Fiber is of the most modern type, able to resist Microbending

The radiation curable Radiation curable Supercoatings is applied Wet on Wet.

The Secondary Coating is a Colored Secondary, wherein the clear Secondary Base Coat is mixed in line with a Color Concentrate.

The type of curing lights are: Proprietary Lamps with a metal halide spectrum similar to Fusion D lamps

The number of curing lights is: 3 lamps/20 inch.

The line speed at which the Supercoatings will be applied is approximately 1700 meters/minute.

Step Three

Step Three-Formulating Supercoatings

For the Primary Coating Layer an Oligomer is selected, along with a photoinitiator, antioxidant, two diluent monomers and other additives based on information available. For the Secondary Coating Layer an Oligomer Blend is selected, along with a photoinitiator, antioxidant, two diluent monomers and other additives based on information available to formulate a Clear Secondary Coating. Colorants are formulated to add to the Clear Secondary Coating during in-line mixing. In addition to running the Primary coating and Secondary coating on the Draw tower Simulator operating at 1625 meters/minute, the Multilayer Film DrawDown test method is used to create Supercoatings Film of a Primary Coating Layer with an overcoat of Clear Secondary Coating Layer. The film is removed from the substrate and tested for the properties in Supercoatings.

In addition to using the Multilayer Film DrawDown test method to create Supercoatings Film of a Primary Coating Layer with an overcoat of Clear Secondary Coating Layer, a Multilayer Film DrawDown is made of a Primary Coating Layer and a Colored Secondary made of the Clear Secondary Coating and Colorant.

Example Example Example Example Candidate Primary 3PA1 3PA2 3PA3 3PA4 Coatings Weight Weight Weight Weight Material description Percent Percent Percent Percent Acclaim polyol 4200 57.63 57.63 57.63 57.63 BHT Food Grade 0.1 0.1 0.1 0.1 IPDI 5.12 5.12 5.12 5.12 Dibutyltin Dilaurate 0.03 0.03 0.03 0.03 zinc neodecanoate 0.03 0.15 dodecylbenzene 0.03 0.15 sulfonic acid 2-HEA 2.12 2.09 2.09 1.82 Oligomer Wt. % 65.00 65.00 65.00 65.00 of total formula SR-504D 21.55 21.55 21.55 21.55 SR 339C 9 9 9 9 SR 349D Monomer 1 1 1 1 Irgacure 819 1.5 0.75 0.5 TPO 1.5 0.75 1 IRGANOX 1035 0.6 0.6 0.6 0.6 FF(W&C) TINUVIN 123 0.1 0.1 0.1 0.1 A-189 1.25 1.25 1.25 1.25 Total (due to rounding 100 100 100 100 of significant figures may be +/−0.10 wt. %)

Example Example 3SA1 Example 3SA3 Clear 3SA2 Color oneH Color oneH twoH Candidate Secondary Coating with Optional Color Concentrate Added Clear Secondary Coating Rose Rose Brown Brown Concentrate Secondary Concentrate Secondary Weight Weight Weight Weight percent percent percent percent Clear Base M^(†) 100.00 90.64 75 84.4 75 White 6.8 Red 1.6 6.8 Yellow 8 Orange 0.96 Black 0.8 Rose colored 2° inter. 25 Brown colored 2° inter. 25 Total (due to rounding of significant 100 100 100 100 figures may be +/−0.10 wt. %)

Clear Base M^(†) Ingredients Weight % Oligomer M3^(∴) 20.27 CN120Z 50.00 TPO 1.06 Chivacure 184 0.80 BHT Food Grade 0.50 KIP 100 F 1.06 SR306 MONOMER 15.00 SR 238 MONOMER 9.80 SR-504D 0.50 DC-190 Surfactant 0.68 DC-57 Additive 0.33 Total (due to rounding of significant 100.00 figures may be +/−0.10 wt. %)

Example 3 Continued

Oligomer M3^(∴) is an Oligomer. The ingredients combined to make Oligomer M3 include the following:

Oligomer M3^(∴) Material description Wt. % TDI Type II 21.26 BHT Food Grade 0.05 2-HEA 14.18 Dibutyltin Dilaurate 0.05 Pluracol P1010 64.46 Total (due to rounding of significant 100.00 figures may be +/−0.10 wt. %)

Example Example Example 3SA1 3SA2 3SA3 Clear Color Color oneH oneH twoH Candidate Secondary Coating with Optional Color Concentrate Added Clear Secondary Coating Rose Rose Brown Brown FILTER TYPE Concentrate Secondary Concentrate Secondary Total Base 2° Resin: 100.00 97.66 84.40 96.10 ⁺Total Colorant: 9.36 2.34 15.60 3.90 ^(@)Total Dry Pigment: 4.59 1.15 3.12 0.78 *Photoinitiator %: 2.92 2.65 2.85 2.46 2.81

Example 4

An optical fiber manufacturer wishes to apply a radiation curable Supercoatings for their MULTI-Mode Optical Fiber. The MULTI-Mode Optical Fiber is of the most modern type, able to resist Microbending.

Step One:

The requested Microbending Sensitivity for single mode optical fiber used in this network is as of this writing, still under investigation at 850 nm and 1300 nm. As details develop more Microbending Sensitivity testing will be done.

Step Two

The MULTI-Mode Optical Fiber is of the most modern type, able to resist Microbending

The radiation curable Secondary Coating is applied Wet on Wet Primary Coating.

The line speed at which the Primary Coating and Secondary Coating will be applied is about 200 meters/minute.

The Secondary Coating is a Clear Secondary.

The type of curing lights are 600 w/D Lamps.

The number of curing lights are: 3 in the Primary Coatings area. 3 in the Secondary Coatings Area

Step 3.

For the Primary Coating Layer an Oligomer is selected, along with a photoinitiator, antioxidant, two diluent monomers and other additives based on information available to make a Multi-Mode Coating. For the Secondary Coating Layer an Oligomer Blend is selected, along with a photoinitiator, antioxidant, two diluent monomers and other additives based on information available to formulate a Clear Secondary Coating for Multi-Mode Coating.

Example 4PD1-4PD5

These Examples illustrate Formulator Delta's formulations for the Primary Coating Layer

Ex. Ex. Ex. Ex. Ex. 4PD1 4PD2 4PD3 4PD4 4PD5 Material Description wt. % wt. % wt. % wt. % wt. % Oligomer 2,4-TDI 3.6 3.43 4.34 3.53 3.38 2,6-di-tert-butyl-p-cresol 0.05 0.05 0.04 0.05 0.05 acrylic acid 0.01 0.01 0.02 0.01 0.01 2-HEA 1.48 1.48 1.48 1.3 1.46 ACCLAIM polyol 4200 50.41 50.10 50.00 48.17 50.10 dibutyl tin dilaurate 0.03 0.03 0.03 0.03 0.03 Total Oligomer wt. % 55.58 55.91 55.91 53.09 55.91 ethoxylated nonyl 40.29 40.29 40.29 42.71 40.29 phenol acrylate SR 349D 1.2 1.50 1.50 1.7 1.50 TPO 0.9 0.0 1.60 1.7 1.70 IRGACURE ® 819 0.5 1.70 0.5 IRGANOX 1035 1.5 0.50 0.50 0.3 0.50 TINUVIN 123 0.03 0.10 0.10 0.1 0.10 A-189 0.90 0.9 0.80 0.90 0.90 Total (due to rounding of 100.00 100.00 100.00 100.00 100.00 significant figures may be +/−0.10 wt. %)

The fifth aspect of the instant claimed invention is a multi-mode optical fiber coated with radiation

curable coatings comprising a Primary Coating Layer and a Secondary Coating Layer

wherein the composition of the Primary Coating layer, prior to curing, is selected from the group

consisting of the formulation of Example 4PD5; and

wherein the composition of the Secondary Coating layer, prior to curing, is selected from the group

consisting of the formulations of Examples 2SA4 and 2SB3.

Example 5

This Supercoatings Secondary is formulated from an existing Supercoatings Secondary to meet the needs of a customer that is requesting a product with a higher refractive index to enable them to use installed equipment to ascertain concentricity in their finished coated fiber. The changes from the earlier coating are as follows:

a) include the use of SR-601 at about a 10% level,

b) the use of slightly more TPO, from 0.5% to 0.75%,

c) slightly more Chivacure 184, from 2% to 2.5%,

d) the elimination of IBOA and SR-306, which is replaced by about 15% of PEA.

Example Example Example 5SA1 5SA2 5SA3 Function in Wt. % in Wt. % in Wt. % in Formula COMPONENT formula formula formula oligomer Oligomer M3^(∴) 28.1 25.1 35.0 epoxy acrylate CN-110 37.4 39.4 37.4 acrylate monomer HDDA 5.2 5.2 5.2 acrylate monomer SR-601 10.3 10.3 10.3 acrylate monomer PEA 14.75 15.75 7.85 Photo initator TPO 0.75 0.75 0.75 Photo initiator Chivacure 184 2.5 2.5 2.5 Stabilizer Irgacure 1035 0.5 0.5 0.5 silicon surfactant DC-190 0.33 0.33 0.33 Silicon Surfactant DC-57 0.17 0.17 0.17 Total (due to 100 100 100 rounding of significant figures may be +/−0.10 wt. %)

Oligomer M3^(∴) is an Oligomer. The ingredients combined to make Oligomer M3 include the following:

Oligomer M3^(∴) Material description Wt. % TDI Type II 21.26 BHT Food Grade 0.05 2-HEA 14.18 Dibutyltin Dilaurate 0.05 Pluracol P1010 64.46 Total (due to rounding of significant 100.00 figures may be +/−0.10 wt. %)

Example 6

This shows the combination of Primary Coating and Secondary Coating in each of the listed Supercoatings.

Secondary Coating Primary Example Example Example Coating 2SA4 Example 2SB3 3SA1 5SA1 Exam- Super- Supercoatings Supercoating Supercoatings ple coatings 013128 112057 081556 1PA2 072727 Exam- Super- Supercoatings Supercoatings Supercoatings ple coatings 062551 062752 072054 1PB3 041656 Exam- Super- Supercoatings Supercoatings Supercoatings ple coatings 062551100510 062752100510 072054100510 1PC1 0416100510 Exam- Super- Supercoatings Supercoatings Supercoatings ple coatings 013110 112010 081510 2 Alpha 072710 Exam- Super- Supercoatings Supercoatings Supercoatings ple coatings 062510 062710 072010 2 Beta 041610

All references, including publications, patent applications, and patents, cited herein are hereby incorporated by reference to the same extent as if each reference were individually and specifically indicated to be incorporated by reference and were set forth in its entirety herein.

The use of the terms “a” and “an” and “the” and similar referents in the context of describing the invention (especially in the context of the following claims) are to be construed to cover both the singular and the plural, unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.

An embodiment embodiments of this invention are described herein, including the best mode known to the inventors for carrying out the invention. Variations of those an embodiment embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the invention to be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context. 

1-5. (canceled)
 6. A multi-mode optical fiber coated with radiation curable coatings comprising a Primary Coating Layer and a Secondary Coating Layer, wherein the composition of the Primary Coating layer, prior to curing, is selected from the group consisting of the formulation: 55.91 wt. % of an oligomer prepared by reaction of: 3.38 wt. % of 2,4-toluene diisocyanate, 0.05 wt. % of 2,6-di-tert-butyl-p-cresol, 0.01 wt. % of acrylic acid, 1.46 wt. % of 2-hydroxyethyl acrylate, 50.10 wt. % of polypropylene glycol, MW=4200, and 0.03 wt. % of dibutyltin dilaurate; 40.29 wt. % ethoxylated nonyl phenol acrylate; 1.50 wt. % of bisphenol A ethoxylate diacrylate; 1.70 wt. % of 2,4,6-trimethylbenzoyldiphenylphosphine oxide type photoinitiator; 0.50 wt. % of hindered phenol antioxidant; 0.10 wt. % of bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidyl)sebacate; and 0.90 wt. % of γ-mercaptopropyltrimethoxysilane; and wherein the composition of the Secondary Coating layer, prior to curing, is selected from the group consisting of the formulations of group (a), (b), (c) and (d); wherein said formulations (a), (b), (c) and (d) are defined as follows: (a) 28.78 wt. % of an oligomer prepared by reaction of: 21.26 wt. %, by weight of the oligomer, of an 80/20 blend of the 2,4- and 2,6-isomer of toluene diisocyanate, 0.05 wt. %, by weight of the oligomer, of 2,6-di-tert-butyl-4-methylphenol, 14.18 wt. %, by weight of the oligomer, of 2-hydroxyethyl acrylate, 0.05 wt. %, by weight of the oligomer, of dibutyltin dilaurate, and 64.46 wt. %, by weight of the oligomer, of polypropylene glycol, MW=1000; 38.42 wt. % of difunctional bisphenol A-based epoxy acrylate oligomer; 7.2 wt. % of isobornyl acrylate; 8.15 wt. % of 2-phenoxyethyl acrylate; 5.76 wt. % of tripropylene glycol diacrylate; 4.27 wt. % of 1,6-hexanediol diacrylate; 2.43 wt. % of a blend, wherein said blend consists essentially of 35 wt. % of aromatic acid acrylate half ester and 65 wt. % of ethoxylated trimethylolpropane triacrylate; 1 wt. % of 2,4,6-trimethylbenzoyldiphenylphosphine oxide type photoinitiator; 0 wt. % of bis(2,4,6-trimethylbenzoyl)phenylphosphine oxide; 3 wt. % of 1-hydroxycyclohexyl-phenyl ketone; 0.5 wt. % of hindered phenol antioxidant; 0.33 wt. % of a blend, wherein said blend consists essentially of, 40 to 70 wt. % of dimethyl, methyl(propyl(poly(ethylene oxide)(propylene oxide))acetate)siloxane, 30 to 60 wt. % of poly(ethylene oxide propylene oxide)monoallyl ether acetate, and less than 9 wt. % of polyether polyol acetate; and 0.17 wt. % of dimethyl, methyl(propyl(poly(ethylene oxide))acetate)siloxane; (b) 30.00 wt. % of an oligomer prepared by reaction of 21.26 wt. %, by weight of the oligomer, of an 80/20 blend of the 2,4- and 2,6-isomer of toluene diisocyanate, 0.05 wt. %, by weight of the oligomer, of 2,6-di-tert-butyl-4-methylphenol, 14.18 wt. %, by weight of the oligomer, of 2-hydroxyethyl acrylate, 0.05 wt. %, by weight of the oligomer, of dibutyltin dilaurate, and 64.46 wt. %, by weight of the oligomer, of polypropylene glycol, MW=1000; 40.00 wt. % of epoxy diacrylate; 7.5 wt. % of isobornyl acrylate; 8.5 wt. % of 2-phenoxyethyl acrylate; 6 wt. % of tripropylene glycol diacrylate; 4.5 wt. % of 1,6-hexanediol diacrylate; 0.5 wt. % of hindered phenol antioxidant; 0.0 wt. % of bis(2,4,6-trimethylbenzoyl)phenylphosphine oxide; 0.5 wt. % of 2,4,6-trimethylbenzoyldiphenylphosphine oxide type photoinitiator; 2 wt. % of 1-hydroxycyclohexyl-phenyl ketone; 0.33 wt. % of a blend, wherein said blend consists essentially of, 40 to 70 wt. % of dimethyl, methyl(propyl(poly(ethylene oxide)(propylene oxide))acetate)siloxane, 30 to 60 wt. % of poly(ethylene oxide propylene oxide)monoallyl ether acetate, and less than 9 wt. % of polyether polyol acetate; and 0.17 wt. % of dimethyl, methyl(propyl(poly(ethylene oxide))acetate)siloxane; (c) 20.27 wt. % of an oligomer prepared by reaction of: 21.26 wt. %, by weight of the oligomer, of an 80/20 blend of the 2,4- and 2,6-isomer of toluene diisocyanate, 0.05 wt. %, by weight of the oligomer, of 2,6-di-tert-butyl-4-methylphenol, 14.18 wt. %, by weight of the oligomer, of 2-hydroxyethyl acrylate, 0.05 wt. %, by weight of the oligomer, of dibutyltin dilaurate, and 64.46 wt. %, by weight of the oligomer, of polypropylene glycol, MW=1000; 50.00 wt. % of epoxy diacrylate; 1.06 wt. % of 2,4,6-trimethylbenzoyldiphenylphosphine oxide type photoinitiator; 0.80 wt. % of 1-hydroxycyclohexyl phenyl ketone; 0.50 wt. % of 2,6-di-tert-butyl-4-methylphenol; 1.06 wt. % of a blend, wherein said blend consists essentially of, 70 wt. % of oligo[2-hydroxy-2-methyl-1-[4(1-methyl-vinyl)phenyl]propanone] and 30 wt. % of 2-hydroxy-2-methyl-1-phenylpropanone; 15.00 wt. % of tripropylene glycol diacrylate; 9.80 wt. % of 1,6-hexanediol diacrylate; 0.50 wt. % of ethoxylated(4) nonyl phenol acrylate, MW=450; 0.68 wt. % of a blend, wherein said blend consists essentially of, 40 to 70 wt. % of dimethyl, methyl(propyl(poly(ethylene oxide)(propylene oxide))acetate)siloxane, 30 to 60 wt. % of poly(ethylene oxide propylene oxide)monoallyl ether acetate, and less than 9 wt. % of polyether polyol acetate; and 0.33 wt. % of dimethyl, methyl(propyl(poly(ethylene oxide))acetate)siloxane; and (d) 28.1 wt. % of an oligomer prepared by reaction of: 21.26 wt. %, by weight of the oligomer, of an 80/20 blend of the 2,4- and 2,6-isomer of toluene diisocyanate, 0.05 wt. %, by weight of the oligomer, of 2,6-di-tert-butyl-4-methylphenol, 14.18 wt. %, by weight of the oligomer, of 2-hydroxyethyl acrylate, 0.05 wt. %, by weight of the oligomer, of dibutyltin dilaurate, and 64.46 wt. %, by weight of the oligomer, of polypropylene glycol, MW=1000; 37.4 wt. % of a difunctional bisphenol A-based epoxy acrylate oligomer; 5.2 wt. % of 1,6-hexanediol diacrylate; 10.3 wt. % of ethoxylated 4 bisphenol A diacrylate; 14.75 wt. % of 2-phenoxyethyl acrylate; 0.75 wt. % of 2,4,6-trimethylbenzoyldiphenylphosphine oxide type photoinitiator; 2.5 wt. % of 1-hydroxcyclohexyl phenyl ketone; 0.5 wt. % of hindered phenol antioxidant; 0.33 wt. % of a blend of 40 to 70 wt. % of dimethyl, methyl(propyl(poly(ethylene oxide)(propylene oxide))acetate)siloxane, 30 to 60 wt. % of poly(ethylene oxide propylene oxide)monoallyl ether acetate, and less than 9 wt. % of polyether polyol acetate; and 0.17 wt. % of dimethyl, methyl(propyl(poly(ethylene oxide))acetate)siloxane. 